Abstract:Thermally stable CeO2 cubes and nanospheres were synthesized and modified by sulfation treatment. Non-sulfated CeO2 cubes and nanospheres did not exhibit good catalytic performance for selective catalytic reduction of NOx with NH3 (NH3-SCR), but mainly contributed towards an undesired side reaction of NH3 oxidation above 350 degrees C. Based on the structural, morphological and physicochemical characterization, it was observed that CeO2 nanospheres comprising small crystallites could easily release active oxygen species, which resulted in strong NH3 oxidation. However, sulfation treatment greatly improved the catalytic performance of NH3-SCR on both CeO2 cubes and nanospheres. Sulfated CeO2 catalysts did not contribute to significant NH3 oxidation due to the inhibited reducibility of Ce4+ coordinated with the surface sulfates. The adsorbed ammonia could be activated on Bronsted acid sites generated by the formation of surface Ce-2(SO4)(3) species, while gaseous NOx could be activated on separate surface sites of Ce4+. The presence of separate reaction sites for NH3 and NOx is believed to be important for the improved catalytic performance of SCR reaction. Sulfated CeO2 cubes outperformed sulfated CeO2 nanospheres in the entire test temperature window (200-500 degrees C). The improved performance of sulfated CeO2 cubes appears to be related to surfaces with abundant Bronsted acid sites and relatively weak reducibility of Ce4+. These fundamental findings contribute to a better mechanistic understanding needed for designing efficient CeO2-based NOx reduction catalysts in the future.

Sulfation Effect of Ce/TiO2 Catalyst for the Selective Catalytic Reduction of NOx with NH3: Mechanism and Kinetic Studies

Investigation on the redox/acidic features of bimetallic MOF-derived CeMOx catalysts for low-temperature NH3-SCR of NOx

In Situ DRIFTS Studies of NH3-SCR Mechanism over V2O5-CeO2/TiO2-ZrO2 Catalysts for Selective Catalytic Reduction of NOx

The Contradictory Impact of Sulfation on a CeOx/TiO2 NH3-SCR Catalyst: A Combined Experimental and DFT Study

The Contradictory Impact of Sulfation on a CeO<sub><i>x</i></sub>/TiO<sub>2</sub> NH<sub>3</sub>-SCR Catalyst: A Combined Experimental and DFT Study

The Contradictory Impact of Sulfation on a CeO x /TiO 2 NH 3 -SCR Catalyst: A Combined Experimental and DFT Study

Temperature sensitivity of the selective catalytic reduction (SCR) performance of Ce-TiO2 in the presence of SO2

The role of cerium in the improved SO2 tolerance for NO reduction with NH3 over Mn-Ce/TiO2 catalyst at low temperature

Novel effect of SO2 on the SCR reaction over CeO2: Mechanism and significance

Effect of SO 2 introduction into CeO 2 on its surface acidity and redox property for the selective catalytic reduction of NO with NH 3

Promotional Effects on NH3-SCR Performance of CeO2–SnO2 Catalysts Doped by TiO2: A Mechanism Study

The Enhanced Performance of Ceria with Surface Sulfation for Selective Catalytic Reduction of No by Nh3

A mechanistic investigation of the selective catalytic reduction of NOx with NH3 over supported CeO2/TiO2 catalysts

Investigation of the Effect of Cu Addition on the SO2-resistance of a CeTi Oxide Catalyst for Selective Catalytic Reduction of NO with NH3

Activating low-temperature NH3-SCR catalyst by breaking the strong interface between acid and redox sites: A case of model Ce2(SO4)3-CeO2 study

Relationship between SO2 poisoning effects and reaction temperature for selective catalytic reduction of NO over Mn–Ce/TiO2 catalyst

Mechanism of Selective Catalytic Reduction of NOx with NH3 over CeO2-WO3 Catalysts

Shape Dependence and Sulfate Promotion of CeO2 for Selective Catalytic Reduction of NO with NH3

Preparation and characterization of CeO2/TiO2 catalysts for selective catalytic reduction of NO with NH3

Effects of Anaerobic SO2 Treatment on Nano-Ceo2 of Different Morphologies for Selective Catalytic Reduction of NOx with NH3

New Understanding of the Promotional Nature of SO2 on Ce-Based Oxide Catalysts for Selective Catalytic Reduction of NO X with NH3