Abstract:Hydrogel features can be designed and optimized using different crosslinking agents to meet specific requirements. In this regard, the present work investigates the physico-chemical features of cellulose-based hydrogels, designed by using different epoxy crosslinkers from the same glycidyl family, namely epichlorohydrin (ECH), 1,4-butanediol diglycidyl ether (BDDE), and trimethylolpropane triglycidyl ether (TMPTGE). The effect of the crosslinker's structure (from simple to branched) and functionality (mono-, bi- and tri-epoxy groups) on the hydrogels' features was studied. The performances of the hydrogels were investigated through the gel fraction, as well as by ATR-FTIR, DVS, SEM, DSC, and TG analyses. Also, the swelling and rheological behaviors of the hydrogels were examined. The advantages and limitations of each approach were discussed and a strong correlation between the crosslinker structure and the hydrogel properties was established. The formation of new ether bonds was evidenced by ATR-FTIR spectroscopy. It was emphasized that the pore size is directly influenced by the crosslinker type, namely, it decreases with the increasing number of epoxy groups from the crosslinker molecule, i.e., from 46 ± 11.1 µm (hydrogel CE, with ECH) to 12.3 ± 2.5 µm (hydrogel CB, with BDDE) and 6.7 ± 1.5 µm (hydrogel CT, with TMPTGE). The rheological behavior is consistent with the swelling data and hydrogel morphology, such as CE with the highest Qmax and the largest pore size being relatively more elastic than CB and CT. Instead, the denser matrices obtained by using crosslinkers with more complex structures have better thermal stability. The experimental results highlight the possibility of using a specific crosslinking agent, with a defined structure and functionality, in order to establish the main characteristics of hydrogels and, implicitly, to design them for a certain field of application.

Strengthened Cellulosic Gels by the Chemical Gelation of Cellulose Via Crosslinking with TEOS

Thermally Induced Gel from Cellulose/naoh/peg Solution: Preparation, Characterization and Mechanical Properties

High-strength Cellulose/poly(ethylene Glycol) Gels.

Thermal Gelation Of Cellulose In A Naoh/Thiourea Aqueous Solution

Graphene-Oxide-Sheet-Induced Gelation of Cellulose and Promoted Mechanical Properties of Composite Aerogels

Preparation and properties of cellulose ionic gel

Gelation Behavior of Cellulose in NaOH/urea Aqueous System Via Cross-Linking

Cellulose-rich Oleogels Prepared with an Emulsion-Templated Approach

Enhanced electromechanical performance of bio-based gelatin/glycerin dielectric elastomer by cellulose nanocrystals

Tailoring the Structure and Physico-Chemical Features of Cellulose-Based Hydrogels Using Multi-Epoxy Crosslinking Agents

Cellulose Aerogel Beads and Monoliths from CO2-based Reversible Ionic Liquid Solution

Combined experiments and molecular simulations for understanding the thermo-responsive behavior and gelation of methylated glucans with different glycosidic linkages

Synthesis and Performance Evaluation of a New Kind of Gel Used As Water Shutoff Agent

A “bird nest” bioinspired strategy deployed for inducing cellulose gelation without concomitant dissolution

Freeze-thaw and Solvent-Exchange Strategy to Generate Physically Cross-Linked Organogels and Hydrogels of Curdlan with Tunable Mechanical Properties.

Cellulose films from the aqueous DMSO/TBAH-system

Novel cellulose-gelatin composite films made from self-dispersed microgels: Structure and properties

The Measurement of Molecular Interactions, Structure and Physical Properties of Okara Cellulose Composite Hydrogels Using Different Analytical Methods.

Solvent-tuned multiple self-assembly of a new sugar-appended gelator.

Fabrication and Characterization of Chemical Crosslinked Cellulose Fiber by Dissolving Cellulose in Alkali Urea Aqueous Solvent

Unique Gelation Behavior of Cellulose in Naoh/Urea Aqueous Solution