Abstract:The tension-compression yield asymmetry caused by the strengthening of Mg-Zn-Gd-Zr alloy due to extrusion deformation is an important issue that must be addressed in its application. In this study, the effects of loading direction on the tensile and compressive mechanical behaviors of Mg-5Zn-2Gd-0.2Zr alloy were systematically investigated. As the loading angle (the angle between the loading direction and the extrusion direction) increases from 0° to 30°, 45°, 60° and 90°, the tensile yield strength decreases more significantly than the compressive yield strength. Consequently, the tension-compression yield asymmetry is gradually improved. Additionally, the ultimate compressive strength decreases more markedly than the ultimate tensile strength with the increment of the loading angle. In tensile tests conducted at 0°, 30° and 45°, two distinct stages of decreasing strain hardening rates are typically observed. For the 60° and 90° tensile tests, one unusual ascending stage of strain hardening rate is observed. For all compressive tests, three stages of strain hardening are consistently noted; however, the increment in strain hardening rate caused by {10–12} extension twinning decreases with the increasing loading angle. A model combining loading angle and Schmid factor distribution was established. The calculated results indicate that the dominant deformation modes during the yielding process also vary significantly with the loading conditions. This clarification highlights the differences in yield strength variations between tension and compression. Finally, an analysis of the plane trace and crack propagation direction near the fracture surface reveals the fracture mechanisms associated with tensile and compressive tests at different loading directions. This study promotes understanding of the mechanical behaviors of Mg-5Zn-2Gd-0.2Zr alloy under different loading directions, and helps to thoroughly elucidate the anisotropic effects of texture on the mechanical properties of magnesium alloys.

Grain Morphology and Orientation Effect on the High-Temperature Tensile Behavior of Directionally Solidified Magnesium Alloy

High-temperature tensile properties and deformation mechanism of polycrystalline magnesium alloys with specifically oriented columnar grain structures

Study on Tensile Behavior at Various Temperatures of the Mg-7Gd-5Y-1Nd-2Zn-0.5Zr Alloy

Effects of the Growth Rate on Microstructures and Room Temperature Mechanical Properties of Directionally Solidified Mg-5.2Zn Alloy

Effect of Tensile Direction on Mechanical Properties and Microstructural Evolutions of Rolled Mg-Al-Zn-Sn Magnesium Alloy Sheets at Room and Elevated Temperatures

Tensile Properties, Texture Evolutions and Deformation Anisotropy of As-Extruded Mg-6Zn-1Zr Magnesium Alloy at Room and Elevated Temperatures

Effects of temperature and strain rate on deformation behaviors of an extruded Mg-5Zn-2.5Y-1Ce-0.5Mn alloy

Effect of Loading Direction on Tensile-Compressive Mechanical Behaviors of Mg-5Zn-2Gd-0.2Zr Alloy with Heterogeneous Grains

Microstructure evolution, strengthening mechanisms and deformation behavior of high-ductility Mg−3Zn−1Y−1Mn alloy at different extrusion temperatures

Unveiling the mechanical response and deformation mechanism of extruded Mg-2.5Nd-0.5Zn-0.5Zr alloy sheet under high-temperature tensile

Microstructures and Mechanical Properties of Extruded Mg-1mn-3.5y and Mg-1mn-1y-2.5nd Alloys

Influence of Texture and Grain Size on the Room-Temperature Ductility and Tensile Behavior in a Mg–Gd–Zn Alloy Processed by Rolling and Forging

Grain size and orientation affected deformation inhomogeneity and local damage of hot-deformed Al-Zn-Mg alloy

Room-Temperature Strengthening, Portevin-Le Chatelier Effect, High-Temperature Tensile Deformation Behavior, and Constitutive Modeling in a Lightweight Mg-Gd-Al-Zn Alloy

The high-temperature deformation and microstructural evolution mechanism of Mg-Gd-Y-Zn-Zr alloy formed by CMT arc additive forming

Effect of Heat Treatment on Dynamic Recrystallization Behaviors and Mechanical Properties of Mg–2.7Nd–0.5Zn–0.8Zr Alloy

A comprehensive analysis on microstructure evolution of Mg-5.65Zn-0.66Zr alloy during hot deformation

Effect of Twin and Grain Size Strengthening on Tensile Properties of a Multi-Directionally Impact Forged Mg–Gd–Y Alloy

Understanding the Deformation Behaviours of Mg Alloys with Dispersed Non-Basal Grain-Embedded Orientation Heterostructures

Microstructure and Mechanical Properties of Extruded Mg-Zn-Y Alloy

Microstructural evolution, phase constitution and mechanical properties of directionally solidified Mg-5.5Zn-xGd (x = 0.8, 2.0, and 4.0) alloys