Abstract:While carbon-fiber-reinforced polymers (CFRPs) are widely used in the aerospace industry, they are not able to disperse current from lightning strikes because their conductivity is relatively low compared to metallic materials. As such, the undispersed current can cause the vaporization or delamination of the composites, threatening aircraft safety. In this paper, finite element models of lightning damage to CFRPs were established using commercial finite element analysis software, Abaqus, with the user-defined subroutines USDFLD and HEAVEL. The influences of factors such as the structural geometry, laminate sequence, and intrinsic properties of CFRPs on the degree of damage to the composites are further discussed. The results showed that when a current from lightning is applied to the CFRP surface, it mainly disperses along the fiber direction in the outermost layer. As the length of the CFRP increases, the injected current has a longer residence time in the material due to the increased current exporting distance. Consequently, larger amounts of current accumulate on the surface, eventually leading to more severe damage to the CFRP. This damage can be alleviated by increasing the thickness of the CFRP, as the greater overall resistance makes the CFRP a better insulator against the imposed current. This study also found that the damaged area increased as the angle between the first two layers increased, whereas the depth of the damage decreased due to the current dispersion between the first two layers. The analysis of the electrical conductivity of the composite suggested that damage in the fiber direction will be markedly reduced if the conductivity in the vertical fiber direction increases approximately up to the conductivity of the fiber direction. Moreover, increasing the thermal conductivity along the fiber direction will accelerate the heat dissipation process after the lightning strike, but the influence of the improved thermal conductivity on the extent of the lightning damage is less significant than that of the electrical conductivity.

Experimental Investigation of the Damage of GFRP under 10/350 Μs Simulated Lightning Currents

Experimental and Numerical Analysis of Damage Mechanisms for Carbon Fiber-Reinforced Polymer Composites Subjected to Lightning Strikes

Damage Analysis for Carbon Fiber/epoxy Composite Exposed to Simulated Lightning Current

Experimental study of the damage behaviour of laminated CFRP composites subjected to impulse lightning current

Study on the Factors Influencing the Damage Modes of Carbon Fiber-Reinforced Polymer Composites with a Fastener under Lightning Strike Conditions

Damage Characteristics of CFRP Laminates Subjected to Multiple Lightning Current Strike

Damage Simulation and Experiment of Carbon Fiber Composites Subjected to Lightning Current

Understanding Lightning Strike Induced Damage Mechanism of Carbon Fiber Reinforced Polymer Composites: an Experimental Study

Lightning Induced-damage Characteristics of CFRP Composites under Lightning Arc

Lightning strike-induced dynamic conduction characteristics and damage behavior of carbon fiber-reinforced polymer composites

Resistance Behaviour of Carbon Fibre-Reinforced Polymers Subjected to Lightning Strikes: Experimental Investigation and Application

Damage Investigation of Carbon-Fiber-Reinforced Plastic Laminates with Fasteners Subjected to Lightning Current Components C and D

Finite Element Analysis of Lightning Damage Factors Based on Carbon Fiber Reinforced Polymer

Quantitative Experimental Study of Mechanical Effects of Carbon Fiber Composites under Impulse Lightning Current

Testing of Conductive Carbon Fiber Reinforced Polymer Composites Using Current Impulses Simulating Lightning Effects

Influence of Grounding Modes on the Damage of Carbon Fiber Reinforced Plastics Subjected to Lightning Strikes

Experimental study for the effect of hole notched in fracture mechanics of GLARE and GFRP composites subjected to quasi-static loading

Dynamic characteristics of carbon fiber reinforced polymer under nondestructive lightning current

Assessment of Delamination Damage in Carbon Fibre Reinforced Polymer Composites with a Fastener Under Multiple Lightning Strike Conditions

Evaluation Method for Lightning Damage of Carbon Fiber Reinforced Polymers Subjected to Multiple Lightning Strikes with Different Combinations of Current Components

Enhanced through-thickness electrical conductivity and lightning strike damage response of interleaved vertically aligned short carbon fiber composites