Abstract:The hydrolysis of AB has been regarded as a kind of secure and efficient method for hydrogen generation. However, the development of economical and stable catalysts with high catalytic activities remains a bottleneck for realizing further industrial application of AB. Herein, high-loading heterostructured Ni/NiO nanoparticles with different Ni/NiO weight ratios anchored on one-dimensional porous MoO x nanorods (denoted as Ni/NiO@MoO x ) have been synthesized and introduced into the hydrolysis of AB for the first time. The Ni/NiO@MoO x -50H catalyst (synthesized under the reduction atmosphere of 50% H2/50% Ar) with an optimal Ni/NiO weight ratio (73.96/26.04) exhibits an excellent catalytic activity for the hydrolysis of AB with the turnover frequency (TOF) value reaching 86.29 molH 2 molNi –1 min–1 at 298 K, which is one of the highest TOF values among the reported non-noble metal catalysts. In addition, on account of high Ni loading weight (29.15 wt %), the hydrogen generation rate of Ni/NiO@MoO x -50H achieves 10,478 mL·min–1 g–1 (35,947 mL·min–1 gNi –1), overtaking most values both in noble and non-noble metal catalysts for the hydrolysis of AB. The bridging effect of NiO steadily connects the Ni and MoO x carrier and promotes great durability of Ni/NiO@MoO x -50H, of which the catalytic activity exhibits not significant degradation in the fifth cycle. The catalysis originated from the metal/metal oxide (Ni/NiO@MoO x ) provides a novel insight into the catalyst design, preparation, and application for chemical hydrogen storage systems.

3D porous Ni–Zn catalyst for catalytic hydrolysis of sodium borohydride and ammonia borane

Synergistic catalysis over Ni/ZrOx for hydrogen production from hydrolysis of ammonia borane

Nanostructured Ni2P As a Robust Catalyst for the Hydrolytic Dehydrogenation of Ammonia–Borane

Hydrogen Generation from Borohydride Hydrolysis on Surface-Alloyed Ni Foam

Heterostructured Ni/NiO Nanoparticles on 1D Porous MoOx for Hydrolysis of Ammonia Borane

Heterostructured Ni/NiO Nanoparticles on 1D Porous MoO x for Hydrolysis of Ammonia Borane

Low-cost ternary Ni–Fe–P catalysts supported on Ni foam for hydrolysis of ammonia borane

Ultrafine RhNi Nanocatalysts Confined in Hollow Mesoporous Carbons for a Highly Efficient Hydrogen Production from Ammonia Borane

Ultrafine Ni-MoOx Nanoparticles Anchored on Nitrogen-Doped Carbon Nanosheets: A Highly Efficient Noble-Metal-Free Catalyst for Ammonia Borane Hydrolysis

Electronic Engineering Induced Ultrafine Non-Noble Nanoparticles for High-Performance Hydrogen Evolution from Ammonia Borane Hydrolysis

Electrospun Bimetallic NiCr Nanoparticles@Carbon Nanofibers as an Efficient Catalyst for Hydrogen Generation from Ammonia Borane

Defective Ehanced Subnano-Rh Catalyst Supported on an Ni@Ni-N-C Substrate for Highly Efficient Hydrolytic Dehydrogenation of Ammonia Borane

Rh‐Ni‐B Nanoparticles as Highly Efficient Catalysts for Hydrogen Generation from Hydrous Hydrazine

High-Surface-Area Co-Cu-B Monolithic Self-Supported Catalyst for Efficient Sodium Borohydride Hydrolysis

Amorphous Nickel Nanofilms for Efficient Hydrogen Generation from ammonia borane

Modulating Electronic Metal‐Support Interactions to Boost Visible‐Light‐Driven Hydrolysis of Ammonia Borane: Nickel‐Platinum Nanoparticles Supported on Phosphorus‐Doped Titania

Ultrasmall Rhodium Nanoclusters Anchored on Nitrogen-Doped Carbon Nanotubes with Embedded Nickel Nanoparticles As Magnetically Recyclable Catalysts for Efficient Ammonia-Borane Hydrolysis

Coupling ultralow-content ruthenium with nickel hydroxide via corrosion engineering for highly efficient hydrogen generation from ammonia borane

Hydrogen Production from Ammonia Borane over PtNi Alloy Nanoparticles Immobilized on Graphite Carbon Nitride

Boosted Reactivity of Ammonia Borane Dehydrogenation over Ni/Ni2P Heterostructure

Remarkably boosting Ru-Ni nanocatalysis via surface/interface regulation for efficient hydrolytic dehydrogenation of ammonia borane