Abstract:Two types of transparent wood composites with anisotropic structure for energy-saving windows were successfully fabricated by infiltration of epoxy resin dispersion containing tungsten-doped vanadium dioxide nanoparticles (W-doped VO2 NPs) into the delignified wood template and subsequent polymerization. The well integration of the epoxy resin, W-doped VO2 NPs, and the pore-structured wood endowed the anisotropic composites with high visible transmittance (68.2% for the composite prepared from longitudinally cut trees (L-composite), 73.3% for the composite prepared from radically cut trees (R-composite)), obviously different mechanical performance (fracture stress of 74.57 MPa (L-composite) and 56.14 MPa (R-composite) and modulus of 1.47 GPa (L-composite) and 1.23 GPa (R-composite)), and low thermal conductivity (0.20 W·m–1 K–1 (L-composite) and 0.32 W·m–1 K–1 (R-composite)). Moreover, these two kinds of W/VO2 transparent wood composites both show an outstanding thermoregulation ability when they are used as windows. A significant amount of heat (from a simulated light source) was reflected by VO2 NPs, and as a result, the indoor temperature of a demo system had a significant slower temperature increase rate when compared with that for a similar system with a common glass panel applied. Novel transparent wood composites combining a low thermal conductivity wood template and thermochromic VO2 NPs provide a potential solution for replacement of heavy, high thermal conductivity, and infrared transparent glass but still meet indoor occupancy view perception.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c06494?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c06494</a>.Top-view SEM images of untreated pine wood and delignified wood, table and distribution figure for the cell wall thickness of pine wood before and after delignification, and XRD patterns of the W-doped VO2 samples with various molar ratios of W/V (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c06494/suppl_file/am0c06494_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

STRUCTURALLY COLORED WOOD COMPOSITE WITH REFLECTIVE HEAT INSULATION AND HYDROPHOBICITY

Reversible Photo-, Thermal-, and Ph-Responsive Functionalized Wood with Fluorescence Emission.

Eco‐Friendly Color Printing Using Transparent Wood Paper

Fabrication of carbon dots-embedded luminescent transparent wood with ultraviolet blocking and thermal insulating capacities towards smart window application

Impact of cellular structure on the thickness and light reflection properties of structural color layers on diverse wood surfaces

Transparent, UV Blocking, and Strong Wood-Based Biocomposites with Isotropic Optical and Mechanical Properties

Powering the Future Green Buildings: Multifunctional Ultraviolet-Shielding Transparent Wood

Transparent Wood Film Incorporating Carbon Dots As Encapsulating Material for White Light-Emitting Diodes

Carbon dots: building a robust optical shield for wood preservation

Encapsulation of thermochromic tetradecyl myristate/methyl red composite via full poplar-based cellulose/lignin/SiO2 framework for preparation of thermochromic wood with thermal response and storage

Preparation of Hydrophobic Optically Transparent Wood via An Efficient UV-Assisted Route

Coloration and Fire Retardancy of Transparent Wood Composites by Metal Ions

Processing bulk wood into a light-permeable passive radiative cooling material for energy-efficient building

Reversible Dual-Stimuli-Responsive Chromic Transparent Wood Biocomposites for Smart Window Applications

Preparation of Photochromic Wood Films Comprising Spiropyran-Based Wood Cellulose Scaffold Realized through Grafting and Densification

Improvement of decorative texture effects, thermal stability, and mechanical properties of Pinus massoniana using a combined dyeing and superhydrophobic modification method

An aesthetic transparent wood resistant to Escherichia coli based on interface optimization

Transparent Wood Composites Fabricated by Impregnation of Epoxy Resin and W-Doped VO 2 Nanoparticles for Application in Energy-Saving Windows

Hydrochromic wood biocomposites for humidity and moisture detection

Scalable aesthetic transparent wood for energy efficient buildings

Laminated Transparent Woods with Adjustable Optical and Enhanced Mechanical Properties