Transparent Wood Composites Fabricated by Impregnation of Epoxy Resin and W-Doped VO 2 Nanoparticles for Application in Energy-Saving Windows

Liangmiao Zhang,An Wang,Tianli Zhu,Zhang Chen,Yupeng Wu,Yanfeng Gao
DOI: https://doi.org/10.1021/acsami.0c06494
2020-07-08
Abstract:Two types of transparent wood composites with anisotropic structure for energy-saving windows were successfully fabricated by infiltration of epoxy resin dispersion containing tungsten-doped vanadium dioxide nanoparticles (W-doped VO<sub>2</sub> NPs) into the delignified wood template and subsequent polymerization. The well integration of the epoxy resin, W-doped VO<sub>2</sub> NPs, and the pore-structured wood endowed the anisotropic composites with high visible transmittance (68.2% for the composite prepared from longitudinally cut trees (L-composite), 73.3% for the composite prepared from radically cut trees (R-composite)), obviously different mechanical performance (fracture stress of 74.57 MPa (L-composite) and 56.14 MPa (R-composite) and modulus of 1.47 GPa (L-composite) and 1.23 GPa (R-composite)), and low thermal conductivity (0.20 W·m<sup>–1</sup> K<sup>–1</sup> (L-composite) and 0.32 W·m<sup>–1</sup> K<sup>–1</sup> (R-composite)). Moreover, these two kinds of W/VO<sub>2</sub> transparent wood composites both show an outstanding thermoregulation ability when they are used as windows. A significant amount of heat (from a simulated light source) was reflected by VO<sub>2</sub> NPs, and as a result, the indoor temperature of a demo system had a significant slower temperature increase rate when compared with that for a similar system with a common glass panel applied. Novel transparent wood composites combining a low thermal conductivity wood template and thermochromic VO<sub>2</sub> NPs provide a potential solution for replacement of heavy, high thermal conductivity, and infrared transparent glass but still meet indoor occupancy view perception.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c06494?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c06494</a>.Top-view SEM images of untreated pine wood and delignified wood, table and distribution figure for the cell wall thickness of pine wood before and after delignification, and XRD patterns of the W-doped VO<sub>2</sub> samples with various molar ratios of W/V (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c06494/suppl_file/am0c06494_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology
What problem does this paper attempt to address?
The problem that this paper attempts to solve is to develop a new type of energy - saving window material. Specifically, the author prepared two transparent wood - based composites (W/VO\(_2\)-TPW) with anisotropic structures by mixing tungsten - doped vanadium dioxide nanoparticles (W - doped VO\(_2\) NPs) with epoxy resin and infiltrating them into delignified wood templates. These composites are intended to replace traditional glass windows to achieve better heat insulation performance and infrared shielding effect, thereby reducing building energy consumption. ### Main problems: 1. **Improving the heat insulation performance of windows**: Due to its high thermal conductivity, traditional glass windows require more cooling in summer to maintain indoor temperature, resulting in energy waste. However, transparent wood - based composites can effectively reduce heat transfer due to their low thermal conductivity, thus saving energy. 2. **Enhancing infrared shielding ability**: W - doped VO\(_2\) NPs will undergo a phase change at a specific temperature, changing from a semiconductor state to a metal state, thereby reflecting a large amount of infrared radiation. This characteristic enables the composites to effectively block infrared rays at high temperatures, further improving the energy - saving effect of the windows. 3. **Maintaining good visible light transmittance**: Although nanoparticles are added, the composites still need to maintain a high visible light transmittance to ensure natural indoor lighting. ### Solutions: - **Material preparation**: Remove lignin from wood by delignification treatment, retain its porous structure, then infiltrate the mixture of W - doped VO\(_2\) NPs and epoxy resin into the wood, and finally carry out polymerization and curing. - **Performance optimization**: Optimize the optical, mechanical and thermal properties of the composites by adjusting the concentration of W - doped VO\(_2\) NPs, so that they have excellent heat insulation and infrared shielding properties while maintaining a high visible light transmittance. - **Experimental verification**: Through the simulated solar radiation experiment, the energy - saving effect of the W/VO\(_2\)-TPW composites in practical applications was verified. The results show that they are significantly superior to ordinary glass and transparent wood (TPW) in terms of heat insulation and infrared shielding. ### Conclusion: The W/VO\(_2\)-TPW composites prepared by the above methods not only have good transparency and optical properties, but also possess excellent heat insulation and infrared shielding capabilities, and are expected to become important candidates for future energy - saving window materials.