Nitrogen-Doped Carbon-Encased Bimetallic Selenide for High-Performance Water Electrolysis

Cao Junhui,Wang Kexin,Chen Jiayi,Lei Chaojun,Yang Bin,Li Zhongjian,Lei Lecheng,Institute of Zhejiang University - Quzhou,Ostrikov Kostya

DOI: https://doi.org/10.1007/s40820-019-0299-4

IF: 26.6

2019-01-01

Nano-Micro Letters

Abstract:Demand of highly efficient earth-abundant transition metal-based electrocatalysts to replace noble metal materials for boosting oxygen evolution reaction (OER) is rapidly growing. Herein, an electrochemically exfoliated graphite (EG) foil supported bimetallic selenide encased in N-doped carbon (EG/(Co, Ni)Se2–NC) hybrid is developed and synthesized by a vapor-phase hydrothermal strategy and subsequent selenization process. The as-prepared EG/(Co, Ni)Se2–NC hybrid exhibits a core–shell structure where the particle diameter of (Co, Ni)Se2 core is about 70 nm and the thickness of N-doped carbon shell is approximately 5 nm. Benefitting from the synergistic effects between the combination of highly active Co species and improved electron transfer from Ni species, and N-doped carbon, the EG/(Co, Ni)Se2–NC hybrid shows remarkable electrocatalytic activity toward OER with a comparatively low overpotential of 258 mV at an current density of 10 mA cm−2 and a small Tafel slope of 73.3 mV dec−1. The excellent OER catalysis performance of EG/(Co, Ni)Se2–NC hybrid is much better than that of commercial Ir/C (343 mV at 10 mA cm−2 and 98.1 mV dec−1), and even almost the best among all previously reported binary CoNi selenide-based OER electrocatalysts. Furthermore, in situ electrochemical Raman spectroscopy combined with ex situ X-ray photoelectron spectroscopy analysis indicates that the superb OER catalysis activity can be attributed to the highly active Co–OOH species and modified electron transfer process from Ni element.