X. Q. Liang,Y. Q. Wang,J. T. Zhao,S. H. Wu,X. B. Feng,K. Wu,J. Y. Zhang,G. Liu,J. Sun
DOI: https://doi.org/10.1016/j.msea.2019.138259
IF: 6.044
2019-01-01
Materials Science and Engineering A
Abstract:The microstructural evolution and hardness of He-irradiated Nb/Zr crystalline/crystalline multilayers with a wide range of layer thickness h from 5 to 100 nm were investigated under three different ion dose Phi of 1.0 x 10(16), 1.0 x 10(17) and 5.0 x 10(17) ions.cm(-2) at room temperature. Careful microstructural examinations found the occurrence of a radiation-induced amorphization phenomenon near the interface. Besides, He bubbles were distributed within the Nb layers and at the interface. Both the amorphization and He bubble distribution were highly dependent on h and Phi, which caused the mechanical properties sensitive to h and Phi. With reducing h, the hardness of as-deposited Nb/Zr multilayers showed a maximum at h = 10 nm. While the He-irradiated samples manifested a hardening behavior at Phi = 1.0 x 10(16) ions.cm(-2), a softening behavior at Phi = 5.0 x 10(17) ions.cm(-2) and a transition from hardening to softening at Phi = 1.0 x 10(17) ions.cm(-2) with reducing h. These strengthening behaviors were rationalized by a coupling effect of dislocation-amorphous and dislocation-bubble interactions. Modified mechanistic models based on interactions of dislocations with obstacles were employed to quantitatively describe the underlying strengthening mechanisms.
What problem does this paper attempt to address?