Influence of tunable interfaces on radiation tolerance and nanomechanical behavior of homogeneous multi-nanolayered Al1.5CoCrFeNi high entropy alloy films

Guo Pu,Liwei Lin,Ding Ren,Kefu Gan,Bin Liu,Zongbiao Ye,Yihan Wang,Kun Zhang,Zhiming Li,Bo Liu

DOI: https://doi.org/10.1016/j.jnucmat.2022.153734

IF: 3.555

2022-04-01

Journal of Nuclear Materials

Abstract:Introducing high-density defect sinks, e.g., grain boundaries (GBs) and interfaces, to capture helium (He) atoms and irradiation-induced defects under He+ irradiation is a promising strategy for constructing novel nuclear-materials with enhanced radiation tolerance. To understand the vital roles of GBs and interfaces on the irradiation response in high entropy alloys (HEAs), high-density GBs and homogeneous interfaces between layers were firstly introduced into multi-nanolayered Al1.5CoCrFeNi HEA films by tailoring the nominal monolayer thickness (h) ranging from 2 nm to 100 nm. The multi-nanolayered HEA films were then irradiated by 60 keV He+ at a fluence of 1 × 1017 cm−2. The results show that the He bubbles with size of 1-2 nm were preferentially distributed along the GBs within the films and the phase structure kept stable in the irradiated HEA films with less interfaces (such as h = 100 nm). This suggests that the He bubbles mainly distributed at GB sinks due to the high-density GB intersections acted as dominant defect-sinks to trap He atoms. While both the distribution of He bubbles throughout the interfaces and the partial BCC→FCC phase transformation due to radiation-induced segregation were disclosed by introducing numerous interfaces in the irradiated multi-nanolayered HEA films (h = 10 nm and 30 nm). The corresponding intrinsic mechanism of He behavior was elucidated based on the interactions between the He defects and the nano-GBs or homogeneous interfaces. The underlying mechanism of irradiation-induced phase transformation was explained by the relief of compression stress and the radiation-induced segregation behavior by vacancy-flux. Also, the roles of interfaces and GBs on the irradiation swelling and nano-mechanical properties of the HEA films were also revealed by the systematic investigations.

materials science, multidisciplinary,nuclear science & technology