Abstract:In situ irradiations with 30 keV He+ have been performed on W–0.5 wt % ZrC at 823 and 1073 K. Detailed characterization showed that the dislocation loops around the ZrC particles with the size range of ∼120–370 nm were lower in density and smaller than that far away from these particles. The larger the sizes of ZrC particles, the lower the density and smaller the sizes of dislocation loops around the particles would be. In contrast, the higher density of dislocation loops with larger sizes around the ZrC particles with the size range of ∼20–60 nm was displayed. The interaction between a ⟨100⟩ dislocation line and a ⟨100⟩ dislocation loop was in situ observed and investigated by molecular dynamics simulation for the first time. The reacted ⟨100⟩ dislocations with the orthogonal Burgers vectors are more likely to be responsible for the interaction than that with the parallel geometry. The interaction required the generation of glissile 1/2⟨111⟩ dislocation segments, which acted as an "intermediate bridge" between the reacted sessile dislocations. The current results will be of benefit to deeply understand the irradiation behavior of the W–ZrC alloy acting as the plasma-facing materials for the application of fusion reactors.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsaem.1c03915.SRIM profile of irradiation damage and injected helium concentration as a function of irradiation depth, g·b = 0 invisibility criterion close to [001] to determine the types of dislocation loops, and geometry for dislocation line l2 and dislocation loop n under two-beam diffraction conditions g = 110 and g = 11̅0 close to [001] (PDF)This article has not yet been cited by other publications.

A mechanism for basal vacancy loop formation in zirconium

Two-dimensional Vacancy Platelets As Precursors for Basal Dislocation Loops in Hexagonal Zirconium

Dislocation-enhanced Experimental-Scale Vacancy Loop Formation in Hcp Zirconium in One Single Collision Cascade

An Atomistic Modelling Study of the Properties of Dislocation Loops in Zirconium

Transmission Electron Microscopy Characterization of Dislocation Loops in Irradiated Zirconium

Primary damage production in the presence of extended defects and growth of vacancy-type dislocation loops in hcp zirconium

Atomistically informed dislocation dynamics simultations: Application to dislocation-loop interactions in zirconium

Hydrogen and vacancy clustering in zirconium

TEM Investigation on the Dislocation Loops in Zirconium Alloy by Neutron and Kr+ Ion Irradiation Tests

Dislocation-accelerated void formation under irradiation in zirconium

Formation of < 100 > Vacancy Dislocation Loops from Two-Dimensional Vacancy Platelets in Body-Centered Cubic Iron

Generation of C-Component Edge Dislocations in Α-Zirconium During Neutron Irradiation – an Atomistic Study

New Mechanisms of Helical Dislocation Formation Via the Pinch-off Process Near a Nano-Inhomogeneity

Formation of vacancy dislocation loops from two-dimensional vacancy platelets in body-centered cubic iron

Evolution of Dislocation Loops in 30 keV He + -Irradiated W–0.5% ZrC Alloys: In Situ TEM Observations and Molecular Dynamics Simulations

Direct Observation of Vacancy-Cluster-Mediated Hydride Nucleation and the Anomalous Precipitation Memory Effect in Zirconium.

Study of Point Defect Mobilities in Zirconium During Electron Irradiation in a High-Voltage Electron Microscope

Fundamental Insights into the Mass Transfer Via Full Dislocation Loops Due to Alternative Surface Cuts

Formation of stacking fault pyramid in zirconium

Oxygen vacancy stabilized zirconia (OVSZ); a joint experimental and theoretical study

A stabilization mechanism of zirconia based on oxygen vacancies only