Oxygen Polyvacancies as Conductive Filament in Zirconia: First Principle Simulation
Timofey V. Perevalov,Damir R. Islamov
DOI: https://doi.org/10.1149/ma2017-02/14/859
2017-09-01
ECS Meeting Abstracts
Abstract:ZrO 2 is the high-κ dielectric perspective for nonvolatile memory applications [1]. Currently ZrO 2 is investigated as potential active medium for the Resistive Random Access Memory [2]. One of the wide spread model of resistive effect based on the filament formation/dissociation. The simplest filament model is a chain of oxygen vacancies, i.e. oxygen polyvacancy. The study of oxygen vacancies chain formation possibility (energy benefit) in ZrO 2 and their ability to participate in conduction is of great theoretical and practical interest. The modeling was carried out in the ZrO 2 cubic (c-), tetragonal (t-) and monoclinic (m-) phase. Simulations were performed in terms of the hybrid DFT using a B3LYP functional in the Quantum-ESPRESSO code. The 192-atom c-, t-ZrO 2 , and 96-atom m-ZrO 2 supercells were used to simulate the oxygen polyvacancy. Each subsequent atom removal from the supercell is determined from the point of view of the minimum formation energy. This model reflects a gradual increase in the polyvacancy size. The trap thermal E th and optical E opt ionization energies are estimated by the formulas offered in [3]. The calculated band gap values of 5.7, 6.1 and 5.6 eV for c-, t- and m-ZrO 2 are consistent with the corresponding experimental values 5.1, 5.78, and 5.83 eV [4]. The 4- and 3-fold coordinated (4f and 3f) O vacancy formation energies, 6.11 and 6.17 eV, predict the 4f vacancies prevalence in the real structure. The Kohn–Sham levels of five V O charged states ( q = -2, -1, 0, 1, 2) localized in the band gap indicate that any type of oxygen vacancies can capture both electrons and holes. The second added electron leads either to the singlet (V -2 (s)) or a triplet (V -2 (t)) defect state, and the latter is 0.06 eV lower in energy. The significant depth of negatively charged defect levels indicates a polaronic effect. The defect peaks width lower than 0.1 eV in TDOS spectra indicate the charge localization in space. The charge density spatial distribution of the excess charge also confirms the charge localization. The positive charge is distributed evenly between the nearest Zr atoms. An additional electron leads to a charge density distribution among two closest to each other Zr atoms, and one can say that there is a kind of Zr-Zr bond. The calculated values of E th can be interpreted as the energy gain when the conduction band bottom electron capture onto the defect. The positive E th values indicate that the charge capture to the O vacancy in m-ZrO 2 is energetically favorable. Thus, an oxygen vacancy in the ZrO 2 is the amphoteric defect, it can act as the electron and hole trap, and participate in charge transport. The calculated values are consisted with E th = 1.15 [5] for ZrO 2 , and E th = 1.25 eV, E opt =2.5 eV for the HfO 2 [6]. For V 0 and V + , a good agreement of the calculation and experiment is observed. The O polyvacancy atomic structure in c-, t - and m-ZrO 2 (Fig. 1) shows that each subsequent vacancy forms near the already existing one, and no more than the 2 removed O atoms relate to any Zr atom. One can assume that this result is valid for amorphous ZrO 2 , and the external electric field determines the preferred direction of the vacancies chains growth. This is consistent with the filament model of resistive switching. For t-ZrO 2 , the energetically favorable O polyvacancy atomic structure is a chain along the [100] direction. Each subsequent removal of oxygen atom adds one filled level to the band gap. These levels are distributed on the band gap preferentially localized close to the monovacancy level. The oxygen polyvacancy growth in size yields a broad defective band in the energy spectrum of ZrO 2 filled with electrons. Since, for the single oxygen vacancy, the extra electron forms something like a Zr-Zr bond, one can assume that ZrO 2 can acquire conductivity, which is carried out through the channel of the Zr ions separating the vacancies in this polyvacancy chain. The work was supported by the Russian Science Foundation, grant #16-19-00002. The modeling was performed on a cluster of the Institute of Semiconductor Physics SB RAS. [1] X.D.Huang, R.P.Shi, P.T.Lai, Appl. Phys. Lett. 104, 162905 (2014). [2] C.-H.Lai, H.-W. Chen, C.-Y.Liu, Materials 9, 551 (2016). [3] D.Muñoz Ramo, J.L.Gavartin, A.L.Shluger, et al. Phys. Rev. B 75, 205336 (2007). [4] R.H.French, S.J.Glass, F.S.Ohuchi, et al. Phys. Rev. B 49, 5133 (1994). [5] G.Jegert, A.Kersch, W.Weinreich, et al. Appl. Phys. Lett. 96, 062113 (2010). [6] V.A.Gritsenko, T.V.Perevalov, D.R.Islamov, Physics Reports 613, 1 (2016). Figure 1
English Else