Abstract:This study investigates how different sodium silicate SiO2/Na2O MS ratios (0.75, 0.9, and 1.2) affect the hydration behavior of amorphous wollastonitic hydraulic (AWH) binders containing various amounts of Al2O3 content (4, 7, 10, and 12%wt). The effects of and interaction between the MS ratio of the activator and the Al2O3 content of the sample on the hydration reaction and paste performance were investigated. The reaction was followed by calorimetry, and the pastes' compressive strength performances were tested at different curing times (2, 7, and 28 days). The hydrated pastes were characterized by FTIR, thermogravimetry analysis, and X-ray diffraction. The calorimetric results show that a higher Al2O3 cContent and a higher MS ratio result in a longer induction period. In terms of paste performance, an increase of the Al2O3 coupled with an activation with a 1.2 MS ratio results in a lower compressive strength after 28 days of hydration; the results range from 76 to 52 MPa. A decrease of the MS ratio to 0.9 allowed the obtention of a narrower range of results, from 76 to 69 MPa. Even though a decrease of the MS ratio to 0.75 led to higher hydration kinetics and high compressive strength results at early ages, at 28 days of curing, a decrease in compressive strength was observed. This may be a consequence of the fast kinetic of the mixture, since the rapid growth of hydration products may inhibit the dissolution at later ages and increase the porosity of the paste. Moreover, the high Al intake in the hydration product, facilitated by the high sodium content of the activator, promotes the formation of a higher number of calcium aluminate silicate hydrate structures (C-A-S-H) to the detriment of calcium silicate hydrate structures (C-S-H), decreasing the compressive strength of the samples. The TGA results indicate that the samples hydrated with the MS075 solution resulted in a higher number of hydrated products at early ages, while the samples hydrated with the MS09 and MS1.2 solutions exhibit a steady increase with curing time. Hence, an equilibrium in the hydration kinetic promoted by Si saturation-undersaturation appears to be fundamental in this system, which is influenced by both the MS ratio and the Al(OH)4- content in solution. The results of this study suggest that for this type of binder, optimal performance can be achieved by decreasing the MS ratio to 0.9. This composition allows for a controlled kinetic and overall higher compressive strength results in pastes produced with this AWH precursor.

Use of Γ-Al2o3 to Prevent Alkali-Silica Reaction by Altering Solid and Aqueous Compositions of Hydrated Cement Paste

Mitigating alkali-silica reaction through metakaolin-based internal conditioning: New insights into property evolution and mitigation mechanism

The effect of meta-halloysite on alkali–aggregate reaction in concrete

Factors Affecting Kinetics and Gel Composition of Alkali–Silica Reaction in Alkali-Activated Slag Mortars

Al(SO4)(OH)·5H2O Stemming from Complexation of Aluminum Sulfate with Water-Soluble Ternary Copolymer and further Stabilized by Silica Gel as Effective Admixtures for Enhanced Mortar Cementing

Expansion and Mitigation of Alkali-Silica Reaction in Binary Blended Concrete Confining Potentially Reactive Aggregates

Assessment of Various Mitigation Strategies of Alkali-Silica Reactions in Concrete Using Accelerated Mortar Test

Suppressing of alkaline aggregate reaction (AAR) through waterproofing of concrete surface, aggregates, and mortars

Alkali-silica reaction resistance versus susceptibility of geopolymer binders

Calcium nitrate effectively mitigates alkali–silica reaction by surface passivation of reactive aggregates

Mitigating the Drying Shrinkage and Autogenous Shrinkage of Alkali-Activated Slag by NaAlO2

Rheology and alkali-silica reaction of alkali-activated slag mortars modified by fly ash microsphere: a comparative analysis to OPC mortars

Concrete containing recycled concrete coarse aggregate and crushed glass sand: Mitigating the effect of alkali–silica reaction

Role of Aluminum and Lithium in Mitigating Alkali-Silica Reaction—A Review

Influence of Silica Modulus on the Activation of Amorphous Wollastonitic Hydraulic Binders with Different Alumina Content: Study of Hydration Reaction and Paste Performance

Production of amorphous aluminosilicate and vaterite from acid leaching of hydrated cement paste

Study on the Effect and Mechanism of Alkali–Silica Reaction Expansion in Glass Concrete

Alkali-Silica Reaction and Residual Mechanical Properties of High-Strength Mortar Containing Waste Glass Fine Aggregate and Supplementary Cementitious Materials

Alkali-silica Reaction and Strength of Concrete with Pretreated Glass Particles As Fine Aggregates

Effect of pore solution alkalinity on alkali–silica reaction (ASR) in metakaolin‐based geopolymer

Role of the structure of synthetic Al(OH)3 on the properties of sulfoaluminate cement-based materials