FTIR and XPS Studies on the Effect of Ca2+on the Fotation of Monazite by Octyl Hydroxamic Acid
Rong-xiang Liu,Zhan-feng Yang,Jie Li,Zhao Cao,Qiang Li,Ji-chuan L.I
DOI: https://doi.org/10.3964/j.issn.1000-0593(2024)10-2959-09
2024-01-01
Spectroscopy and spectral analysis
Abstract:The monazite flotation system often has many associated minerals such as calcite, fluorite, and dolomite, These associated minerals will dissociate large amount of Cat in the monazite ore, and Ca often affects the pulp flotation environment. In this paper, the surface properties of monazite were studied by FTIR and XPS when Ca affected the flotation of monazite by octyl hydroxamic acid. The research method is mainly through the solution chemical calculation of Ca the flotation test of monazite, and the surface infrared spectroscopy (FTIR) and X-ray photoelectron spectroscopy (XPS) of monazite under flotation conditions, The solution chemical calculation of Ca shows that an aqucous solution with increased pH value. Cat exists in an ionic state, hydroxyl complex, and hydroxide compound, respectively. At the same time, the dominant components are Ca and Ca(OH) at pH between 7 and 8. The results of monazite flotation showed that OHA could not fully float monazite without adding Ca", and the recovery rate was 75. 37%. When the pH is (8 +/- 0.5), and the dosage of Ca Ca is 3X 10 mol L., the flotation performance of OHA on monazite can be significantly improved, and the recovery rate reaches 96.48%. According to the solution chemistry calculation. Ca(OH) is the dominant component of activated monazite. When the Ca dose is greater than 3x10 mol 1. the flotation recovery rate decreases greatly, indicating that the further increase of C a<^> 2+ dose inhibits the flotation of monazite. Only a certain dose of C a<^> 2+ effectively promotes the flotation of monazite, which may be attributed to the consumption of OHA concentration by C a<^> 2+ dose, which in turn affects the flotation of monazite, Infrared spectroscopy analysis showed that under the action of C a<^> 2+ * two key new peaks appeared in the spectrum, one was the N / O * H bending vibration peak at 1 * 454c * m <^> - 1 the other was the ON stretching vibration peak at 880c * m <^> - 1 . and the organic peaks at 2. 974 and 2 928 cm. The CH, and CH, peaks were significantly enhanced, and these groups appeared to indicate that chemical adsorption occurred and the adsorption intensity was greater than that of pure monazite adsorption of OHA, XPS analysis showed that the relative content of N element on the surface of monazite was 0.61% when only OHA was used to adsorb monazite. In comparison, the relative content of N element on the surface of monazite was 2. 36% when OHA was used to adsorh monazite after Ca treatment, It can be concluded that C * a <^> 24 will promote the adsorption of OHA on the surface of monazite, It can be seen from the peak fitting that the addition of C a<^> 2+ cacts with C a (OH) <^> + to form O Ca OH groups on the cleavage surface of monazite to form O Ca OH groups, which can be used as a new adsorption site for adsorbing OHA. At the same time, the cerium atom of monazite and the two oxygen atoms on OHA form a five-membered chelate, which also acts as an adsorption site, It is concluded that there can be two adsorption sites on the surface of monazite, The active sites of Ca and Ce atoms on the surface of monazite can adsorb OHA, which is beneficial to the adsorption of OHA on the surface of monazite and forms a more uniform and dense OHA hydrophobic adsorption layer. This is why the performance of C a<^> 2+ in OHA flotation of monazite is improved. This study helps to enrich the activation theory of metal ions in pulp and also confirms that effective mineral flotation separation depends not only on the strength of collector mineral interaction but also on the chemical properties of the flotation solution to a large extent, Utilizing or controlling the surface reaction should be the main goal of developing a more efficient and economical flotation process,