Improving Ethanol Sensitivity of ZnSnO3 Sensor at Low Temperature with Multi-Measures: Mg Doping, Nano-Tio2 Decoration and UV Radiation

Xiuyu Wang,Heng Li,Xuantong Zhu,Mengzhen Xia,Tao,Binxin Leng,Wen Xu

DOI: https://doi.org/10.1016/j.snb.2019.126745

2019-01-01

Abstract:A kind of ZnSn(OH)(6) crystalline precursor composed of micro- and nano-sized particles with two different morphologies was synthesized by co-precipitation method with the presence of triethanolamine (TEOA) as functional reagent. Zn1-xMgxSn(OH)(6) samples (0 <= x <= 0.5) were prepared by doping Mg2+ ions in the synthesis process of ZnSn(OH)(6) precursor. Experimental results reveal that both the morphology and size of ZnSn(OH)(6) particles can be changed by TEOA and Mg2+ ions, but not changed by dehydration at high temperature with the formation of Zn1-xMgxSnO3 samples. When x is 0.1, the effect of Mg2+ ions on the morphology and size of ZnSn(OH)(6) particles is not remarkable, but the ethanol sensitivity of the resulting ZnSnO3 sample at a low temperature of 80 degrees C is significantly improved by Mg2+ ions at the conditions of nano-TiO2 decoration and UV radiation. The ethanol response of the composite sample (ZM(0.1)SO-T-10) is as high as ca. 149 at 500 ppm concentration, and its corresponding response and recovery time is about 4 s and 80 s, respectively. Furthermore, the sensor with ZM(0.1)SO-T-10 also shows a good selectivity and long-term stability. Possible reasons for the superior ethanol sensitivity at low temperature were discussed.