Effects of chopped carbon fiber on the forming, structure and mechanical properties of CCF/SiC composites fabricated by SLS and RMI
Tianlong Liu,Lixia Yang,Zhaofeng Chen,Guoqiang Wen,Lijun Xiong,Ce Sun,Mengmeng Yang,Qiong Wu,Kai Liu
DOI: https://doi.org/10.1002/adem.202300442
IF: 3.6
2023-06-22
Advanced Engineering Materials
Abstract:Silicon carbide (SiC) composites have been fabricated by selective laser sintering (SLS) combined with reactive melt infiltration (RMI) using SiC powder mixed with various contents (0∽32 vol%) of chopped carbon fiber (CCF) as reinforcement phase and carbon source. The introduction of an appropriate amount of CCF could reduce the shrinkage and step effect caused by slicing, improving the forming quality of the CCF/SiC preforms after pyrolysis. Meanwhile, as a carbon resource, CCF could react with molten silicon to form the β‐SiC, improving the mechanical properties of CCF/SiC composites. The result showed that the CCF/SiC powder showed excellent fluidity, and the angle of repose of the CCF/SiC powder was 32‐40 ° when the proportion of CCF was less than 24 vol%. The shrinkage of CCF/SiC preforms was lower than 1.74 % and 1.94 % along the non‐additive and additive manufacturing directions, respectively. The apparent porosity of CCF/SiC preforms attained the lowest of 47.3 % and the bulk density reached a maximum of 1.35 g/cm3 when the CCF content was 8 vol%. Compared without CCF, the bending strength and fracture toughness of the CCF/SiC composites improved from 137.9 MPa and 2.69 MPa·m1/2 to 177.1 MPa and 3.10 MPa·m1/2, respectively. This study is believed to provide a new strategy for additive manufacturing of high‐performance CCF/SiC composites with high CCF content by SLS. This article is protected by copyright. All rights reserved.
materials science, multidisciplinary