Abstract:Objective: In this study, new dimethacrylate monomer SiMA without Bisphenol A (BPA) structure was synthesized and used as base resin of dental composite materials with the aim of reducing human exposure to BPA derivatives. Methods: SiMA was synthesized through ring-opening addition reaction between 1,3-bis[2(3,4-epoxycyclohex-1-yl)ethyl]tetra-methyldisiloxane and methacrylic acid, and its structure was confirmed by FT-IR and (1)H NMR spectra. SiMA was mixed with TEGDMA (50/50, wt/wt) and photoinitiation system (0.7 wt% of CQ and 0.7 wt% of DMAEMA) to form resin system. Experimental composite EC was then prepared by SiMA based resin loading with BaAlSiO2 microfillers (72wt%). Double bond conversion (DC) was determined by FT-IR analysis. Volume shrinkage (VS) was measured through variation of density before and after irradiation. Water sorption (WS) and solubility (SL) were obtained until the mass variation of polymer in distilled water kept stable. Flexural strength (FS) and modulus (FM) of the polymer were measured using a three-point bending set up. Extract of composite was used to evaluate its cytotoxic effect on humane dental pulp cells, and relative growth rate (RGR) was obtained by CCK-8 assay. Bis-GMA/TEGDMA (50/50, wt/wt) resin system and universal dental restorative materials 3M ESPE Filtek™ Z250 were used as references for neat resin system and composite material, respectively. Results: FT-IR and (1)H NMR spectra showed that structure of SiMA was the same as designed. For the neat resin systems: DC of SiMA based resin was higher than that of Bis-GMA based resin (p<0.05); SiMA based resin had lower VS than Bis-GMA based resin; WS of SiMA based resin was lower than that of Bis-GMA based resin (p<0.05), while SL of SiMA based resin was nearly the same as that of Bis-GMA based resin (p>0.05); FS and FM of SiMA based resin were lower than those of Bis-GMA based resin (p<0.05). For the composite materials: DC of EC was higher than that of Z250 (p<0.05); EC and Z250 had same VS; WS of EC was lower than that of Z250 (p<0.05), and SL of EC was higher than that of Z250 (p<0.05); FS and FM of EC were lower than those of Z250 (p<0.05); RGRs of EC were lower than those of Z250 after the cells were incubated with relative extract for 24h and 48h (p<0.05), while after being incubated for 72 h, RGR of EC and Z250 had no obvious difference (p>0.05). Significance: SiMA had potential to replace Bis-GMA as base resin of dental composite materials. However, formulation of SiMA based resin and composite should be optimized in terms of mechanical strength to satisfy the requirements of resin based dental materials for clinical application.

Preparation of Experimental Resin Composites with an Anti-Adhesion Effect Against S. Mutans Using Branched Silicone Methacrylate.

Preparation of dental resin composites with anti-bacterial adhesion against Streptococcus mutans using fluorinated and silicon containing dimethacrylates

Antibacterial Activity and Bonding Ability of an Orthodontic Adhesive Containing the Antibacterial Monomer 2-Methacryloxylethyl Hexadecyl Methyl Ammonium Bromide.

Antibacterial Effect of a Resin Incorporating a Novel Polymerizable Quaternary Ammonium Salt MAE-DB Against Streptococcus Mutans.

Effect of an Antibacterial Monomer on the Antibacterial Activity of a Pit-and-Fissure Sealant.

Synthesis of none Bisphenol A structure dimethacrylate monomer and characterization for dental composite applications

Mechanical and Antimicrobial Properties of Boron Nitride/Methacrylic Acid Quaternary Ammonium Composites Reinforced Dental Flowable Resins

Bacterial responses to temperature and substrate concentration during the Newfoundland spring bloom

Antibacterial Activity of a Modified Unfilled Resin Containing a Novel Polymerizable Quaternary Ammonium Salt MAE-HB

The Antifungal Effects and Mechanical Properties of Silver Bromide/cationic Polymer Nano-Composite-modified Poly-methyl Methacrylate-Based Dental Resin

In Vitro Antibacterial Activity of a Novel Resin-Based Pulp Capping Material Containing the Quaternary Ammonium Salt MAE-DB and Portland Cement.

Development of Novel Polymerizable Antibacterial Monomer and Its Antibacterial Effects on Dental Adhesive

The Mechanical and Antibacterial Properties of Boron Nitride/Silver Nanocomposite Enhanced Polymethyl Methacrylate Resin for Application in Oral Denture Bases

Microtensile bond strength, 4-point bending and nanoleakage of resin-dentin interfaces: Effects of two matrix metalloproteinase inhibitors

Structural biology: Electron crystallography goes 3D with MicroED

Anti-Microbial Effect of AgBr-NP@CTMAB on Streptococcus Mutans and Assessment of Surface Roughness Hardness and Flexural Strength of PMMA

Development of antibacterial dual-cure dental resin composites via tetrapod-shaped zinc oxide incorporation

Engineering Interfacial Integrity with Hydrolytic-Resistant, Self-Reinforcing Dentin Adhesive

Effects of surface properties of polymer-based restorative materials on early adhesion of Streptococcus mutans in vitro

Lateral and anterior view to tensor fold and supratubal recess.

Characterization of dental light-curing resin composites incorporating multiple modified low-shrink monomers