Aqueous and mechanical exfoliation, unique properties, and theoretical understanding of MoO3 nanosheets made from free-standing α-MoO3 crystals: Raman mode softening and absorption edge blue shift
Hongfei Liu,Yongqing Cai,Mingyong Han,Shifeng Guo,Ming Lin,Meng Zhao,Yongwei Zhang,Dongzhi Chi
DOI: https://doi.org/10.1007/s12274-017-1733-x
IF: 9.9
2018-02-02
Nano Research
Abstract:Crystalline α-MoO3 belts consisting of nanosheets stacked along their [010] axes were synthesized via thermal vapor transport of MoO3 powders at elevated temperatures. The MoO3 belts were millimeters in length along their [001] axes and tens to hundreds of micrometers in width along their [100] axes. Mechanical and aqueous exfoliations of the belts to form two-dimensional (2D) nanosheets were processed via the scotch-tape and bovine serum albumin (BSA) assisted methods, respectively. Upon scotch-tape exfoliation, the Raman features of MoO3 exhibited monotonic decreases in intensity as the thickness was gradually fell to approach that of a 2D nanosheet. Most Raman features eventually disappeared when a monolayer nanosheet was produced, except for the Mo–O–Mo stretching mode (Ag) at ~818 cm−1, which was accompanied by mode-softening of up to 5 cm−1. This mode softening, hitherto not reported for 2D α-MoO3 nanosheets, can be attributed to lattice relaxations that are validated here via theoretical density functional perturbation theory calculations. The BSA-assisted exfoliation products exhibited a blueshift in the α-MoO3 nanosheet absorption edge; they also revealed an absorption peak at 3.98 eV that can be attributed to their intrinsic exciton absorptions. These observations, together with the facile synthesis of high-purity α-MoO3 crystals, illuminate the possibility of further 2D α-MoO3 nanosheet production and lattice dynamic studies.
materials science, multidisciplinary,chemistry, physical,physics, applied,nanoscience & nanotechnology