Lithium Borate Containing Bifunctional Binder to Address Both Ion Transporting and Polysulfide Trapping for High-Performance Li-S Batteries.

Lei Zhong,Yudi Mo,Kuirong Deng,Shuanjin Wang,Dongmei Han,Shan Ren,Min Xiao,Yuezhong Meng

DOI: https://doi.org/10.1021/acsami.9b09604

IF: 9.5

2019-01-01

ACS Applied Materials & Interfaces

Abstract:A slightly cross-linked lithium borate containing single ion-conducting polymer (LBSIP) as a bifunctional binder for lithium sulfur batteries is designed and fabricated via one-step thiol-ene click reaction. The LBSIP binder exhibits an over 600 mN mm-1 of the maximum peeling strength between sulfur cathode and aluminium foil, together showing a high lithium ions diffusion coefficient of 2.1×10-12 cm2 s-1. Owing to the unique electron-donating groups, the binder can provides a good ionic conductive network and dramatically enhanced polysulfides-trapping feature. The strong interaction between electron-donating groups of LBSIP with Li2S6 was confirmed by 7Li-NMR analysis and density-functional theory calculation. The cathode using LBSIP binder exhibited high Coulombic efficiency of ~100%, and initial specific capacity of 712 mAh g-1 with a capacity fading rate of 0.06% per cycle after 500 cycles at 0.5 C. Even at a high current rate of 2 C, the reversible capacity of over 500 mAh g-1 was still obtained. However, the capacity of the cathode using PVDF binder decreased to 331 mAh g-1 after 180 cycles at 0.5 C. This work is very attractive for the rational design of functional binders for Li-S batteries with both ion-transporting and polysulfide-trapping features.