Medium Dielectric Constant And Low-Loss Ptfe Composites Filled With Mgo-Lif Co-Doped Li2tio3 Particles

Hao Wang,Hui Yang,Jianxi Tong,Qilong Zhang

DOI: https://doi.org/10.1002/app.47980

IF: 3

2019-01-01

Journal of Applied Polymer Science

Abstract:In this work, we presented a simple strategy to fabricate medium dielectric constant and low-loss composites for microwave substrate applications. MgO-LiF co-doped Li2TiO3 (LT) powders were fabricated by the solid-state reaction route and modified by perfluorooctyltriethoxysilane (F8261). The LT/polytetrafluoroethylene (PTFE) composites were fabricated by cold pressing and hot treatment. The XPS and contact angle analysis indicated that the fluorinated group was introduced to LT particle successfully. The effects of modified LT powders content on the dielectric, thermal, and mechanical properties of composites were investigated. As the modified LT content increases, the dielectric constant, dielectric loss, and temperature coefficient of dielectric constant (tau(epsilon)) increase while the bending strength and coefficient of thermal expansion (CTE) decrease, which is attributed to the higher dielectric constant of LT ceramic, more pores, stable tau(epsilon) of LT ceramic, interface defects and low CTE of LT ceramic, respectively. The composites with 60wt % LT exhibit the best microwave dielectric properties: epsilon(r) = 6.8, tan delta = 0.001, tau(epsilon) = -29.6 ppm degrees C-1 at 8GHz and acceptable coefficient of thermal expansion (28.3 ppm degrees C-1). Therefore, modified LT powders filled PTFE composites are potential materials for high-frequency microwave substrate applications. (c) 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019, 136, 47980.