Mineral Transformation in Treating Low-Grade Bauxite Using the Calcification–carbonization Process and Preparing Cement Clinker with the Obtained Residue

Yanxiu Wang,Ting-an Zhang,Yuhai Zhang,Guozhi Lyu,Weiguang Zhang

DOI: https://doi.org/10.1016/j.mineng.2019.04.031

IF: 5.479

2019-01-01

Minerals Engineering

Abstract:During the Bayer process for alumina production, the molecular formula of the bauxite residue is approximately equivalent to Na2O center dot Al2O3 center dot 1.7SiO(2)center dot nH(2)O. This means that 1 kg of SiO2 in bauxite will produce 1 kg of Al2O3 and 0.608 kg of Na2O in bauxite residue. Thus, the extraction efficiency of alumina is low when processing low-grade bauxite. In addition, it is difficult to utilize bauxite tailings with solid alkali in the structure. In this study, low-grade bauxite was treated using a calcification-carbonization process. A new type of residue (C-C residue) with a different structure from that of traditional bauxite residue was obtained. A cement clinker was prepared with C-C residue as the main ingredient at a dosage of 50%. The experimental results show the alumina extraction efficiency reached 75.82% when processing low-grade bauxite of A/S 3.06 using the calcification-carbonization process. This is higher than the 61.44% of the Bayer process. The main phases of C-C residue [CaCO3, amorphous Ca(4-2x)SixO4, and undecomposed Ca3Al2(SiO4)(OH)(4)] convert into Ca2SiO4, Ca3SiO5, and Ca2FexAl(2-x)O5 after calcination. The calcification-carbonization process combined with cement production helped low-grade bauxite achieve highly efficient and clean alumina production, which is conducive to the sustainable development of alumina industry.