Comparing the Evolution and Deformation Mechanisms of Lamellar and Equiaxed Microstructures in Near Β-Ti Alloys During Hot Deformation

Wei Chen,Yaping Lv,Xiaoyong Zhang,Chao Chen,Y. C. Lin,Kechao Zhou

DOI: https://doi.org/10.1016/j.msea.2019.05.015

2019-01-01

Abstract:This work systematically investigates the microstructural evolution and deformation mechanism of lamellar and equiaxed Ti-55511 alloys during hot deformation. For textural discrepancies, the classical Burgers orientation relationship in lamellar microstructures broke down owing to dynamic recrystallization (DRX) of the α phase during hot deformation, while the intensities of micro-textures increased due to the elongated α phase parallel to the rolling direction. The anisotropies of the mechanical properties in deformed lamellar microstructures were influenced by the DRX of the α phase and inhomogeneous deformation, such as the formation of shear bands. With regard to equiaxed microstructures, dynamic recovery (DRV) of the α phase predominated, forming elongated α grains perpendicular to the loading direction, which increased the anisotropy. However, the anisotropy from DRV was compensated for by the DRX of the β phase. DRV α grains with serrated boundaries promoted the DRX of the β phase due to the accumulation of dislocations. The localized shear band found in the lamellar α plate during spheroidization comprised two ribbon-like {11¯01} twins, which are abreast but non-parallel and play critical roles in the evolution of α phases. The activation of this type of twin is heavily dependent on the aspect ratios of the α phases. These studies provide insight into the deformation behavior of lamellar and equiaxed near β-Ti alloys, which paves the way for the development of ultra-fine-grained microstructures with excellent mechanical properties.