Abstract:The novel ZrIV-based perfluorinated metal-organic framework (PF-MOF) [Zr6O4(OH)4(TFS)6] (ZrTFS) was prepared under solvent-free conditions using the commercially available tetrafluorosuccinic acid (H2TFS) as a bridging ditopic linker. Since H2TFS can be seen as the fully aliphatic and perfluorinated C4 analogue of fumaric acid, ZrTFS was found to be isoreticular to zirconium fumarate (MOF-801). The structure of ZrTFS was solved and refined from X-ray powder diffraction data. Despite this analogy, the gas adsorption capacity of ZrTFS is much lower than that of MOF-801; in the former, the presence of bulky fluorine atoms causes a considerable window size reduction. To have PF-MOFs with more accessible porosity, postsynthetic exchange (PSE) reactions on (defective) MOF-801 suspended in H2TFS aqueous solutions were carried out. Despite the different H2TFS concentrations used in the PSE process, the exchanges yielded two mixed-linker materials of similar minimal formulae [Zr6O4(μ3-OH)4(μ1-OH)2.08(H2O)2.08(FUM)4.04(HTFS)1.84] (PF-MOF1) and [Zr6O4(μ3-OH)4(μ1-OH)1.83(H2O)1.83(FUM)4.04(HTFS)2.09] (PF-MOF2) (FUM2- = fumarate), where the perfluorinated linker was found to fully replace the capping acetate in the defective sites of pristine MOF-801. CO2 and N2 adsorption isotherms collected on all samples reveal that both CO2 thermodynamic affinity (isosteric heat of adsorption at zero coverage, Qst) and CO2/N2 adsorption selectivity increase with the amount of incorporated TFS2-, reaching the maximum values of 30 kJ mol-1 and 41 (IAST), respectively, in PF-MOF2. This confirms the beneficial effect coming from the introduction of fluorinated linkers in MOFs on their CO2 adsorption ability. Finally, solid-state density functional theory calculations were carried out to cast light on the structural features and on the thermodynamics of CO2 adsorption in MOF-801 and ZrTFS. Due to the difficulties in modeling a defective MOF, an intermediate structure containing both linkers in the framework was also designed. In this structure, the preferential CO2 adsorption site is the tetrahedral pore in the "UiO-66-like" structure. The extra energy stabilization stems from a hydrogen bond interaction between CO2 and a hydroxyl group on the inorganic cluster.

Stable Fluorinated 3D Isoreticular Nanotubular Triazole MOFs: Synthesis, Characterization and CO2 Separation

Facile syntheses of tetrahedral imidazolate framework for CO2 separation

Increased CO2 Affinity and Adsorption Selectivity in MOF-801 Fluorinated Analogues

Nitrogen-enriched flexible metal-organic framework for CO2 adsorption

A Series of Cation-Modified Robust Zirconium-Based Metal-Organic Frameworks for Carbon Dioxide Capture

Ultra-high adsorption selectivity and affinity for CO2 over CH4, and luminescent properties of three new solvents induced Zn(II)-based metal-organic frameworks (MOFs)

Three Robust Isoreticular Metal-Organic Frameworks with High-Performance Selective CO 2 Capture and Separation

An ultramicroporous multi-walled metal–organic framework for efficient C2H2/CO2 separation under humid conditions

Increased CO 2 /N 2 selectivity by stepwise fluorination in isoreticular ultramicroporous metal-organic frameworks

Fluorido-bridged iron-based metal-organic frameworks for carbon dioxide capture in humid flue gas

Green Synthesis of MOF-801(Zr/Ce/Hf) for CO 2 /N 2 and CO 2 /CH 4 Separation

Tetrazole-based Porous Metal-Organic Frameworks for Selective CO2 Adsorption and Isomerization Studies.

Reticular Chemistry for Ionic Liquid-Functionalized Metal–Organic Frameworks with High Selectivity for CO 2

New Frontiers of Triazolate-based MOFs: Amine-Functionalization for Enhanced Diluted CO2 Capture Performance

A Series of Metal–Organic Frameworks Built of Triazolate-Trinuclear and Paddlewheel Units: Solid-Solution Framework Approach for Optimizing CO2 Adsorption and Separation

A Microporous Mn(II) MOF Based on 5-(4H-1,2,4-triazol-4-yl) Isophthalic Acid for CO2/N2 Separation

A stable metal-organic framework with suitable pore sizes and rich uncoordinated nitrogen atoms on the internal surface of micropores for highly efficient CO2 capture

A moisture stable metal-organic framework for highly efficient CO2/N2, CO2/CH4 and CO2/CO separation

Efficient C 2 H n Hydrocarbons and VOC Adsorption and Separation in an MOF with Lewis Basic and Acidic Decorated Active Sites

New Frontiers of Trazolate-based MOFs: Amine-Functionalization for Enhanced Diluted CO2 Capture Performance

Two flexible cationic metal-organic frameworks with remarkable stability for CO2/CH4 separation