Abstract:Spent selective catalytic reduction (SCR) catalysts are environmentally hazardous and resource-enriching. In this work, V, W, and As in a spent SCR catalyst was extracted by alkali pressure leaching . Results showed that the V, W, and As were loaded on the anatase TiO 2 crystal grains as amorphous oxides . The optimum pressure leaching conditions were NaOH concentration of 20 wt%, reaction temperature of 180 °C, reaction time of 120 min, L/S of 10 mL/g, and stirring speed of 300 rpm. The leaching efficiency of W, V, and As reached 98.83%, 100%, and 100%, respectively. The experiment revealed the preferential leaching of V and As rather than W, and the leaching mechanisms of V, W, and As were studied through experiment and density functional theory (DFT). The leaching kinetics of W conformed to a variant of the shrinking core model and the leaching process of W is controlled by both chemical reactions and diffusion processes. During the leaching process, Na 2 Ti 2 O 4 (OH) 2 product powder layer was generated, which affects the mass transfer of W. The destruction of the TiO 2 skeleton in the spent SCR catalyst is essential for adequate W extraction, especially for the extraction of W embedded in the TiO 2 lattice. The DFT simulation result indicated that the V and As loaded onto the TiO 2 support are easier to absorb hydroxide ions rather than W, and the leaching reaction energy of V and As was lower than W, As, and V has leaching priority over the leaching of W. Furthermore, an anatase TiO 2 photocatalyst with the {001} crystal surface exposed was successfully prepared from the alkali pressure leaching residue. This work provides theoretical support for the metal leaching and utilization of spent SCR catalysts via alkali pressure leaching.

Efficient Recovery of Scrapped V2O5-WO3/TiO2 SCR Catalyst by Cleaner Hydrometallurgical Process

A Promising Approach to Recover a Spent SCR Catalyst: Deactivation by Arsenic and Alkaline Metals and Catalyst Regeneration

Electrochemical Detoxification and Recovery of Spent SCR Catalyst by In-Situ Generated Reactive Oxygen Species in Alkaline Media

A clean and efficient approach for recovery of vanadium and tungsten from spent SCR catalyst

Effective industrial regeneration of arsenic poisoning waste selective catalytic reduction catalyst: contaminants removal and activity recovery

Environmentally-friendly Harvesting TiO2 Nanospheres and V2O5 Microrods from Spent Selective Catalytic Reduction Catalysts

Formic Acid-Mediated Regeneration Strategy for As-Poisoned V2O5-WO3/TiO2 Catalysts with Lossless Catalytic Activity and Simultaneous As Recycling

Extraction and Separation of Tungsten and Vanadium from Spent V2O5-WO3/TiO2 SCR Catalysts and Recovery of TiO2 and Sodium Titanate Nanorods as Adsorbent for Heavy Metal Ions

Tuning of vanadium valence for value-added recycling and utilization of vanadium from spent Selective Catalytic Reduction Catalysts

Regeneration Of Commercial Scr Catalysts: Probing The Existing Forms Of Arsenic Oxide

Formic Acid-Mediated Regeneration Strategy for As-Poisoned V<sub>2</sub>O<sub>5</sub>-WO<sub>3</sub>/TiO<sub>2</sub> Catalysts with Lossless Catalytic Activity and Simultaneous As Recycling

Comprehensive recovery of W, V, and Ti from spent selective reduction catalysts

Selective leaching of V, W and recycling of TiO2 carrier from waste V2O5-WO3/TiO2 catalysts by mixed alkali liquor

Reconstruction and recovery of anatase TiO 2 from spent selective catalytic reduction catalyst by NaOH hydrothermal method

Iron removal and titanium dioxide support recovery from spent V2O5-WO3/TiO2 catalyst

A promising method to recover spent V2O5–WO3/TiO2 catalyst: treatment by vanadium–titanium magnetite sintering process

An Efficient Plasma Regeneration of As-Poisoned V2o5-Based Catalyst for Simultaneous Poison Removal and Activity Enhancement

A Review on Resource Utilization of Spent V-W-Ti Based Selective Catalytic Reduction Catalysts

Extraction of W, V, and As from spent SCR catalyst by alkali pressure leaching and the pressure leaching mechanism

Insight into Regeneration Mechanism with Sulfuric Acid for Arsenic Poisoned Commercial SCR Catalyst

Recovery of vanadium and tungsten from spent selective catalytic reduction catalyst by alkaline pressure leaching