Abstract:Uniform ceria nanocrystals with good crystallinity and high surface areas were prepared by a facile alcohothermal method with the addition of bases (KOH or NaOH), using Ce(III) or Ce(IV) salt as a starting material. The as-prepared nanocrystals were characterized by means of powder X-ray diffraction (PXRD), transmission electron microscopy (TEM), high-resolution TEM (HRTEM), nitrogen adsorption, thermogravimetry and differential thermal analysis (TG-DTA), Fourier transformation infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS), and ultraviolet and visible spectroscopy (UV-vis). The ceria crystals had controllable sizes from 2.6 to 6.9 nm estimated by the PXRD line broadening analysis. TEM and HRTEM micrographs showed that the as-prepared ceria nanocrystals have a relatively high degree of crystallinity and low degree of conglomeration under high base concentrations. BET specific surface areas of the as-synthesized ceria nanocrystals were very high (103-238 m(2) g(-1)). XPS spectra indicated that the cerium in the nanocrystals was predominantly tetravalent. UV-vis spectra revealed that both the direct and indirect band gap energies of the as-prepared ceria nanocrystals showed a pronounced blue-shifting due to the quantum confinement effect compared to bulk ceria. And the dielectric confinement effect on the band gap energies was also discussed. The as-prepared ceria nanocrystals supported on gamma-Al2O3 exhibited a rather lower conversion temperature (559 K) for CO oxidation to CO2 than that of bulk catalysts prepared by the coprecipitation method. Finally, a hydrolytic alcohothermal mechanism for the preparation of ceria nanocrystals was forwarded.

Enhancement of Catalytic Activity by UV-light Irradiation in CeO2 Nanocrystals

Planar-dependent oxygen vacancy concentrations in photocatalytic CeO2 nanoparticles

Insight into the Contributions of Surface Oxygen Vacancies on the Promoted Photocatalytic Property of Nanoceria

Defect Engineering by Synchrotron Radiation X-rays in CeO2 Nanocrystals.

Coupling Oxygen Ion Conduction to Photocatalysis in Mesoporous Nanorod-Like Ceria Significantly Improves Photocatalytic Efficiency

Surface-Structure Sensitivity of Ceo2 Nanocrystals in Photocatalysis and Enhancing the Reactivity with Nanogold

Embedding Ultrafine and High-Content Pt Nanoparticles at Ceria Surface for Enhanced Thermal Stability.

Enhanced Artificial Enzyme Activities on the Reconstructed Sawtoothlike Nanofacets of Pure and Pr-Doped Ceria Nanocubes

Enhancement effects of surface and bulk oxygen vacancies on the photocatalytic properties of ceria

Controllable synthesis, photocatalytic and electrocatalytic properties of CeO2 nanocrystals

In-situ Fabrication of Ce-rich CeO2 Nanocatalyst for Efficient CO Oxidation

Fabrication of CeO2 nanorods for enhanced solar photocatalysts

Defect Engineering of Ceria Nanocrystals for Enhanced Catalysis via a High-Entropy Oxide Strategy

Improving the Surface Properties of Ceo2 by Dissolution of Ce3+ to Enhance the Performance for Catalytic Wet Air Oxidation of Phenol

Investigation on Mechanism of Photocatalytic Activity Enhancement of Nanometer Cerium-Doped Titania

Facile Alcohothermal Synthesis, Size-Dependent Ultraviolet Absorption, and Enhanced CO Conversion Activity of Ceria Nanocrystals

Sonochemical synthesis of CeO2 nanoparticles with high photocatalytic and antibacterial activities under visible light

Controlled Synthesis of CeO2 Nanorods and Their Promotional Effect on Catalytic Activity and Aging Resistibility for Diesel Soot Oxidation

Improvement of oxide removal rate in chemical mechanical polishing by forming oxygen vacancy in ceria abrasives via ultraviolet irradiation

Enhanced Catalytic Activity of Ceria Nanorods from Well-Defined Reactive Crystal Planes

Cerium Surface-Engineered Iridium Oxides for Enhanced Oxygen Evolution Reaction Activity and Stability