Abstract:Cerium dioxide (CeO2) 2 ) supported palladium (Pd) catalysts have found widespread application in CO oxidation reaction owing to their exceptional catalytic performance. The morphology of the CeO2 2 support dictates the exposed crystal plane, exerting a profound influence on surface structure and redox properties. This is crucial as the atomic arrangement at the surface directly impacts catalytic activity. In this study, a range of CeO2 2 supports with diverse morphologies ( e.g. nano-octahedra, nano-cubes, nano-particles, nano-spheres, and nano-rods) were successfully synthesized through hydrothermal methods and subsequently supported with Pd for CO oxidation. The spherical 1Pd/CeO2-S 2 -S catalyst, revealing exposed (111) + (100) crystal planes, exhibited significantly higher CO catalytic oxidation activity compared to the catalysts with other morphological CeO2 2 supports. The results indicated a positive correlation between the content of Pd x Ce 1-x O 2-y species and catalytic activity. Notably, this species was most abundantly formed in the spherical 1Pd/CeO2-S 2 -S catalyst with exposed (111) + (100) crystal planes. The presence of this active species facilitated the formation of surface defects, increased oxygen vacancy concentration, and enhanced metal-support interaction, consequently greatly improving the CO low-temperature catalytic oxidation activity. Consequently, the oxidation state of Pd in the Pd/CeO2 2 catalyst could be effectively regulated by controlling the exposure of (111) + (100) crystalline surfaces of the CeO2 2 support, further optimizing the catalytic performance of the Pd/CeO2 2 catalytic system.

In-situ Fabrication of Ce-rich CeO2 Nanocatalyst for Efficient CO Oxidation

Novel synthesis of <i>in situ</i> CeO<sub><i>x</i></sub> nanoparticles decorated on CoP nanosheets for highly efficient electrocatalytic oxygen evolution

In-situ Fabrication of Noble Metal Modified (ce, Zr)O2−δ Monolithic Catalysts for CO Oxidation

Efficient CO Oxidation using Co3O4−CeO2 Nanoparticles Supported on Resin–Based Spherical Activated Carbon with Controllable Oxygen Species

Control Synthesis of CeO2 Nanomaterials Supported Gold for Catalytic Oxidation of Carbon Monoxide

In Situ Studies on Ceria Promoted Cobalt Oxide for CO Oxidation

Fabrication and Catalytic Properties of Nanorod-Shaped (pt–pd)/ceo2 Composites

CeO <sub>2</sub> ‐Supported Pt−Au Nanoparticles as Efficient Catalyst for CO Oxidation

Fabrication of supported Pt/CeO2 nanocatalysts doped with different elements for CO oxidation: Theoretical and experimental studies

Increasing Cerium Dispersion Favours Lattice Oxygen Activity of Cobalt Oxides for CO Catalytic Combustion

Fabrication of homogeneously Cu2+/La3+-doped CeO2 nanosheets and their application in CO oxidation

CeO2-Supported Pt-Au Nanoparticles as Efficient Catalyst for CO Oxidation

Cerium Surface-Engineered Iridium Oxides for Enhanced Oxygen Evolution Reaction Activity and Stability

Enhanced Low-Temperature CO Oxidation Activity Through Crystal Facet Engineering of Pd/CeO2 Catalysts

Enhancement of the Activity and Durability in CO Oxidation over Silica-Supported Au Nanoparticle Catalyst Via CeO Modification

In Situ Growth of Ceria on Cerium–Nitrogen–Carbon As Promoter for Oxygen Evolution Reaction

Fabrication Of Ag-Ceo2 Core-Shell Nanospheres With Enhanced Catalytic Performance Due To Strengthening Of The Interfacial Interactions

Atomically Incorporating Ni into Mesoporous CeO2 Matrix via Synchronous Spray-Pyrolysis as Efficient Noble-Metal-Free Catalyst for Low-Temperature CO Oxidation

Strong Electron Coupling Effect at the CoO/CeO 2 Interface Enables Efficient Oxygen Evolution Reaction

Facile Preparation of Well-Dispersed CeO2-ZnO Composite Hollow Microspheres with Enhanced Catalytic Activity for CO Oxidation.

Formation of FeOOH Nanosheets Induces Substitutional Doping of CeO 2− x with High‐Valence Ni for Efficient Water Oxidation