Abstract:A series of mesoporous nanocrystalline Ce-Zr solid solutions with different Ce/Zr ratios were successfully synthesized by the evaporation-induced self-assembly strategy, and were employed as catalytic supports of CuO-based catalysts for CO oxidation. These supports and catalysts were systematically characterized by X-ray powder diffraction (XRD), N-2 physisorption, transmission electron microscopy (TEM), energy-dispersed spectroscopy (EDS) mapping, X-ray photoelectron spectroscopy (XPS), H-2 temperature programmed reduction (H2-TPR), CO2 temperature programmed desorption (CO2-TPD), etc. The catalytic performances toward CO oxidation had been carefully evaluated over these CuO-based catalysts. The effects of various influencing factors, such as the Ce/Zr ratio, mesostructure, redox properties of the support, CuO loading amount and calcination temperature, on the low-temperature catalytic activity had been carefully investigated. The results showed that the catalyst supported on the support with a Ce/Zr ratio of 80/20 exhibited the highest catalytic activity. It was also found that the Ce-Zr solid solution mesoporous catalysts exhibited much higher catalytic activity than the counterparts without evident mesostructure, demonstrating the advantages of the mesoporous catalysts by providing more accessible catalytically active sites. Besides, the mesoporous Ce-Zr solid solution-supported catalysts with excellent redox properties displayed much better catalytic performances than the commercial gamma-Al2O3-supported catalyst. The kinetic study also indicated that the apparent activation energy of the CO oxidation process was greatly affected by the Ce/Zr ratio, mesostructure, and redox properties of the support. Overall, the present CuO-based catalysts with mesoporous nanocrystalline Ce-Zr solid solutions as supports were considered as a series of promising catalysts for CO oxidation.

Enhancement of the Activity and Durability in CO Oxidation over Silica-Supported Au Nanoparticle Catalyst Via CeO Modification

CeO2 Supported Low-Loading Au As an Enhanced Catalyst for Low Temperature Oxidation of Carbon Monoxide

Efficient CO Oxidation using Co3O4−CeO2 Nanoparticles Supported on Resin–Based Spherical Activated Carbon with Controllable Oxygen Species

Influence of Cerium Modification Methods on Catalytic Performance of Au/mordenite Catalysts in CO Oxidation

Dual-functional CeOx fence promoting Au nanocatalyst for CO oxidation under wide working conditions

Morphology effects of nanoscale ceria on the activity of Au/CeO2 catalysts for low-temperature CO oxidation

Halloysite-assisted strong binary oxides-support interactions on multisite catalysts for enhanced stability in preferential CO oxidation

Improvement in ORR Durability of Fe Single-Atom Carbon Catalysts Hybridized with CeO 2 Nanozyme

Carbon-CeO2 Interface Confinement Enhances the Chemical Stability of Pt Nanocatalyst for Catalytic Oxidation Reactions

The Synthesis of SiO2@AuAg@CeO2 Sandwich Structures with Enhanced Catalytic Performance Towards CO Oxidation

The rod-like CeO2 supported by the low-loading Au nanoparticles for the efficient catalytic oxidation of CO at room temperature

Constructing Efficient CuO-Based CO Oxidation Catalysts with Large Specific Surface Area Mesoporous CeO2 Nanosphere Support

Enhanced Low-Temperature CO Oxidation Activity Through Crystal Facet Engineering of Pd/CeO2 Catalysts

Enhancing the Carbon Monoxide Oxidation Performance through Surface Defect Enrichment of Ceria-Based Supports for Platinum Catalyst

Porous stainless-steel fibers supported CuCeFeOx/Zeolite catalysts for the enhanced CO oxidation: Experimental and kinetic studies

Facilely fabricating mesoporous nanocrystalline Ce–Zr solid solution supported CuO-based catalysts with advanced low-temperature activity toward CO oxidation

The Catalytic Performance of Isolated-Dispersed Au on Nanosized CeO2 for CO Preferential Oxidation in H2-rich Stream

Surface pits stabilized Au catalyst for low-temperature CO oxidation

Surface Adsorbed and Lattice Oxygen Activated by the CeO 2 /Co 3 O 4 Interface for Enhancive Catalytic Soot Combustion: Experimental and Theoretical Investigations

Enhancing CO2 Electroreduction with the Metal-Oxide Interface

Enhancing CO Oxidation Activity Via Tuning a Charge Transfer Between Gold Nanoparticles and Supports