A low dielectric polysiloxane with hydro-oleophobicity and improved mechanical properties based on magnolol derivative crosslinker
Guoming Yuan,Hui Yang,Kunxin Wang,WenJie Diao,Enxiang Jiao,Zhijun Liu,Zhao Li,Kun Wu,Jun Shi
DOI: https://doi.org/10.1016/j.porgcoat.2023.107801
IF: 6.6
2023-10-01
Progress in Organic Coatings
Abstract:With the development of the microelectronics industry and the increasing concern for sustainability, there is an urgent need to prepare low dielectric materials from bio-based feedstocks. In this work, an allylated-magnolol (A-M) was synthesized as a crosslinker for fluorinated polymethylhydrosiloxane (F-PMHS) to obtain a low dielectric polysiloxane (M/F-PSO). M/F-PSO exhibited excellent dielectric properties with a dielectric constant of 2.73 and a dielectric loss of 0.0074 at 100 MHz. This was mainly attributed to the synergistic effect of the hard-polarization CF bond and the hindering molecular stacking structure of biphenyl. In addition, M/F-PSO had good hydro-oleophobicity (θwater = 108° and θglycol = 105°), which is brought about by the low surface energy CF3 and the rigid hydrophobic structure of A-M. The water absorption of M/F-PSO was only 0.13 % after 48 h immersion in deionized water. Owing to the introduction of rigid structure and good dispersion of A-M in F-PMHS, the tensile strength of M/F-PSO was up to 5.00 MPa, which is 432 % higher than that of pure polysiloxane (PSO). Moreover, the thermal stability of M/F-PSO was comparable to that of PSO, with an initial decomposition temperature (Td, 5%) as high as 440.30 °C. These results demonstrated the feasibility of introducing renewable bio-resource magnolol into polysiloxane to prepare low dielectric materials with excellent hydro-oleophobicity and mechanical properties.
materials science, coatings & films,chemistry, applied