Abstract:The presence of excessive residual recrystallization structure in the aero-structural part of the Al-Zn-Mg-Cu alloy negatively affects its strength and stress corrosion resistance . To achieve higher service performance, it is significant to reveal the recrystallization behavior of the Al-Zn-Mg-Cu alloy during hot working and subsequent heat treatment. In this work, the isothermal compression tests of an Al-Zn-Mg-Cu alloy were performed at the temperature range 300–450 °C and strain rate range 0.01–10 s −1 . The subsequent heat treatment of the deformed specimens was conducted. The microstructure was characterized by EBSD and XRD techniques. The natural logarithm of Zener-Hollomon parameter (lnZ) was introduced, which increases with the increasing strain rate and decreasing temperature. During hot deformation, CDRX was identified to be the predominant DRX mechanism at high lnZ values, the corresponding recrystallization volume fraction was approximately 15 %. However, at low lnZ values, DDRX becomes the dominant mechanism, the corresponding recrystallization volume fraction was only around 5 %. Moreover, a kinetics analysis was conducted using a low proportion DRX model coupled with lnZ. By comparing the results obtained from finite element simulations with experimental findings, this model was proved to accurately predict the volume fraction of DRX during hot deformation. During the heat treatment process, due to the substantial storage of deformation energy, a significant portion (up to 84.5 %) of SRX was observed under high lnZ conditions. As the lnZ value decreases, the SRX weakens. This weakening is significant enough that under high temperature and low strain rate, the occurrence of SRX becomes extremely unlikely, which can be attributed to the low storage of deformation energy.

Tensile Deformation and Fracture Behaviours of Cold Rolled Cu-3wt.%Ag-0.5wt.%Zr Thin Sheets with Different Annealed Microstructures

Effect of Annealing on the Microstructure, Texture and Tensile Deformation Properties of Cu–3 Wt%ag–0.5 Wt%zr Thin Sheets Rolled at Room and Cryogenic Temperature

The Influence of Warm Rolling Reduction on Microstructure Evolution, Tensile Deformation Mechanism and Mechanical Properties of an Fe-30Mn-4Si-2Al TRIP/TWIP Steel

Reforming Nanostructured CuAg Alloy to Improve Ductility and Electrical Conductivity

Effect of cold rolling on microstructure and mechanical properties of pure Zr

Investigation of size effect on flow stress of Cu-3wt.%Ag-0.5 wt%Zr thin sheets at room and cryogenic temperature based on geometrically necessary dislocation evolution behavior

Effect of Heat Treatments on Microstructures and Tensile Properties of Cu–3 Wt%ag–0.5 Wt%zr Alloy

Revealing the Microstructure Evolution Mechanism and Mechanical Responses of a Novel Al–Zn–Mg–Cu Alloy by Hot Deformation Process

A Constitutive Model Considering Secondary Phase Harden and Size Effect in Plastic Deformation of Cu-3 Wt%ag-0.5 Wt%zr Thin Sheet

Microstructure evolution behavior and mechanical mechanisms in a near α-Zr alloy by cold rolling

Deformation mechanism, orientation evolution and mechanical properties of annealed cross-rolled Mg-Zn-Zr-Y-Gd sheet during tension

The hot deformation characteristics and the associated microstructural evolution of an Al-Cu-Li-Zn alloy studied by constitutive equations and processing maps

Hot Deformation Behavior and Microstructure Evolution of High-Strength Al-Zn-Mg-Cu Alloy

Effect of cryogenic rolling on the microstructure and texture of CuCrZr alloy

Microstructural evolution and mechanical properties of pure zinc subjected to extrusion and caliber rolling

Hot Deformation Behavior and Microstructure Evolution of a Novel High-Zn Containing Al-Zn-Mg-Cu-Zr Alloy

Structure Evolution of Bulk Zr60Cu20Pd10Al10 Amorphous Alloy During Rolling Deformation

Effect of Deformation on Precipitation and the Microstructure Evolution during Multistep Thermomechanical Processing of Al-Zn-Mg-Cu Alloy

New insight of texture and microstructure evolution, and the connections between with tensile performance in as-annealed Al-Cu-Mg-Zr sheet

Recrystallization behavior of an Al-Zn-Mg-Cu alloy during hot deformation and subsequent heat treatment

Effect of cryogenic rolling and multistage thermo-mechanical treatment on the microstructure and properties of the Cu-0.4Cr-0.39Zn-0.1Mg-0.07Zr alloy