Abstract:Crystalline admixture (CA) is an effective self-healing agent for mortar. However, the effects of crack parameters (i.e. crack width and cracking age) and the service environment on the self-healing behavior of CA-containing mortar are not well understood. Herein, the self-healing behavior of mortar containing a self-developed CA was assessed by testing strength recovery, impermeability recovery, and crack closure in pre-cracked specimens. Three initial crack widths (0.2, 0.3, and 0.4 mm), five cracking ages (3, 7, 14, 28, and 56 days), and four external exposure conditions (humidity chamber, air exposure, water immersion, and wet-dry cycles) are investigated. Furthermore, the influence of different external conditions on the healing products at the region of crack and the pore structure of hardened paste containing CA are studied. The results show that adding 4.54% CA into mortar allows rapid healing of 300 μm-wide cracks. Although wider cracks (400 μm) are more difficult to heal, the sorptivity coefficients of the mortars with 400 μm-wide cracks after healing decrease. When the cracks are produced at an earlier age, the pre-cracked specimens have higher recovery ratios of strength and impermeability after healing, and the specimens pe-cracked at a later age still have acceptable compressive strengths after healing. The analysis shows that the strengths and impermeabilities of pre-cracked mortars containing CA exposed to the four external conditions are all recovered. The best self-healing performance is observed for the specimens exposed to water immersion and wet-dry cycles conditions. Somewhat less good self-healing was observed in the specimens exposed to humid chamber condition, while the worst self-healing performance was in the specimens exposed to air exposure condition. This study provides a theoretical basis for the application of novel CAs in cement-based materials.

Effects of External Multi-Ions and Wet-Dry Cycles in a Marine Environment on Autogenous Self-Healing of Cracks in Cement Paste

Interactions between Organic Chelation Agents and Ions in Seawater for Accelerating Self-Healing of Cracks in Cement Paste

Investigating the Self-Healing Performance of Cracked Undersea Constructions

Study on self-healing effect of cement-based materials cracks based on various inorganic minerals

The self-healing of marine concrete cracks based on the synergistic effect of microorganisms and inorganic minerals

Effect of compound mineral capsules on the self-healing performance of cementitious materials under marine environment

A new self-healing agent for accelerating the healing kinetics while simultaneously binding seawater ions in cracked cement paste

Self-healing Properties of Lightweight High-Toughness Cementitious Composites under Dry-Wetting Cycles

Multiple Self-Healing Effects of Water-Absorbing Microcapsules in Cementitious Materials

Assessment of self-healing performance of cement-based materials incorporating ion chelator and industrial wastes

Effect of autogenous crack self-healing on mechanical strength recovery of cement mortar under various environmental exposure

INFLUENCE OF SELF-HEALING ON CHLORIDE ION INGRESS IN CRACKED CONCRETE

Effect of self-healing in closing cracks from the sulfate attack in Portland, supersulfated and alkali-activated cement

Self-healing of early age cracks in cement-based materials by mineralization of carbonic anhydrase microorganism

Development of cementitious capillary crystalline waterproofing agents and durability study of concrete in the presence of chloride with sulfate in aqueous environment

Reactions of self-healing agents and the chemical binding of aggressive ions in sea water: Thermodynamics and kinetics

Synergistic self-healing effect and mechanism of fiber and biological capsule on mortar cracks

Assessment of self-healing behavior of polypropylene fiber-reinforced cement mortar with crystalline admixture: the effects of crack widths, cracking ages, and external conditions

Self-healing of drying shrinkage cracks in cement-based materials incorporating reactive MgO

Effects of magnesia expansive agents on the self-healing performance of microcracks in strain-hardening cement-based composites (SHCC)

Ureolytic MICP-Based Self-Healing Mortar under Artificial Seawater Incubation