Rheological cure characterization of an advanced functional polyurethane
Beatriz Lucio,José Luis de la Fuente
DOI: https://doi.org/10.1016/j.tca.2014.09.012
IF: 3.5
2014-11-01
Thermochimica Acta
Abstract:As part of our continuing study of the curing kinetic and chemorheological analysis of a functional polyurethane (PU) segmented block copolymer formation, in the current paper, we focus on the use the rheological measurements to monitor the entire curing process. The curing reaction was between a metallo-polyol derived of hydroxyl-terminated polybutadiene (HTPB), i.e., (ferrocenylbutyl) dimethylsilane grafted HTPB, and isophorone diisocyanate (IPDI). The evolution of viscoelastic properties, such as storage modulus (G′), loss modulus (G″) and complex viscosity (η*) was recorded in isothermal conditions, at four different temperatures in the range of 50–80°C. The gel times (tgels) were determined by the loss tangent (tanδ) crossover at different frequencies, and the activation energy obtained from them was 69.8kJ/mol. The rheological properties in the region of the gel point have shown that they follow the percolation theory, demonstrating a power law dependence for the shear modulus with a critical exponent n=0.67±0.01, for the higher curing temperatures, 70 and 80°C, and a slightly lower one at lower temperatures, 50 and 60°C. In addition, three different empirical models, among them the Arrhenius and Kiuna rheokinetic models, were used to predict the change in viscosity of this system with the time in the pre-gel region. These results illustrate the rheological curing behavior of this PU resin, its final application being found in the development of advanced energetic composite materials.
chemistry, physical, analytical,thermodynamics