Improving Mechanical Properties of Near Beta Titanium Alloy by High-Low Duplex Aging

Zhaoxin Du,Yan Ma,Fei Liu,Xueping Zhao,Yanfei Chen,Guowei Li,Guolong Liu,Yuyong Chen
DOI: https://doi.org/10.1016/j.msea.2019.03.127
IF: 6.044
2019-01-01
Materials Science and Engineering A
Abstract:A high-low duplex aging (HLDA) heat treatment was carried out on Ti-3.5Al-5Mo-6V-3Cr-2Sn-0.5Fe high-strength beta titanium alloy. The first step of HLDA was carried out at 550 degrees C for 4 h (single aging, SA) followed by the second step aged at 400 degrees C with different aging times. The tensile results show that HLDA can effectively improve the strength and minimize the loss of ductility. During the HLDA, the size of alpha phase obtained from SA is relatively stable in subsequent HLDA owing to low temperature. The omega phase was found in SA alloy, and the content of omega phase gradually decreased. The omega phase transformed to alpha phase with continuous heating during HLDA. The beta ->alpha transformation resulted in an increase in a phase, thus improving the strength. The HLDA exhibited an important advantage: The grain boundaries of alloy showed a good stability, and no visible coarsening was observed, beneficial in enhancing the stability of ductility.
What problem does this paper attempt to address?