Tuning the Morphology and Chemical Distribution of Ag Atoms in Au rich Nanoparticles using Electrochemical Dealloying
Alexandra Dworzak,Paul Paciok,Christoph Mahr,Marc Heggen,Carsten Dosche,Andreas Rosenauer,Mehtap Oezaslan
DOI: https://doi.org/10.1039/d4nr00046c
IF: 6.7
2024-04-23
Nanoscale
Abstract:In contrast to the frequently investigated bulk dealloying, only few studies have focused on the dealloying phenomena of AgAu alloy nanoparticles (NPs). Here, we have investigated the effects of potentiodynamic and potentiostatic dealloying on structure and distribution of residual Ag atoms for Au rich NPs. Two different sizes of Ag rich alloy NPs, 77 ± 26 nm Au 23 Ag 77 and 12 ± 5 nm Au 14 Ag 86 , were prepared. 77 nm Au 23 Ag 77 NPs form a homogeneous alloy, while 12 nm Au 14 Ag 86 NPs show an Ag rich shell – Au rich core arrangement. The two groups of as-prepared NPs were dealloyed either under potentiodynamic (0.2 – 1.3 V RHE ) or potentiostatic (0.9, 1.2, and 1.6 V RHE ) conditions in 0.1 M HClO 4 . For the initial 77 nm Ag 77 Au 23 NPs, both dealloying protocols lead to pore evolution. Interestingly, instead of homogenous Ag distribution, numerous Ag rich regions form and locate near the pores and particle edges. The critical dealloying potential also differs by ~500 mV depending on the dealloying method. The initial 12 nm Au 14 Ag 86 NPs remain dense and solid, but Ag distribution and thickness of Au passivation layer vary between both dealloying protocols. When the Au passivation layer is very thin, the residual Ag atoms tend to segregate to the particle surface after dealloying. Due to the size effect, small NPs are less electrochemically stable and show a lower critical dealloying potential. In this systematic study, we demonstrate that the mobility of Au surface atoms and dealloying conditions control the structure and residual Ag distribution within dealloyed NPs.
materials science, multidisciplinary,physics, applied,nanoscience & nanotechnology,chemistry