Biotemplate-Based Engineering of High-Temperature Stable Anatase TiO2 Nanofiber Bundles with Impregnated CeO2 Nanocrystals for Enhanced Lithium Storage

Yunhong Wei,Han Chen,Hongjun Jiang,Boya Wang,Heng Liu,Yun Zhang,Hao Wu

DOI: https://doi.org/10.1021/acssuschemeng.9b00012

IF: 8.4

2019-01-01

ACS Sustainable Chemistry & Engineering

Abstract:Anatase TiO2 has been deemed as a potential anode material of lithium ion batteries (LIBs) due to its remarkable electrochemical properties, while efficient controlling of the anatase crystal structure is one of the critical approaches to realizing the practical applications of TiO2 anode materials. To this end, we report here a facile biotemplate-engaged design strategy to engineer high-temperature stable anatase TiO2 nanofiber bundles with impregnated CeO2 nanocrystals (TCBs) by taking the advantages of unique chemical and structural characteristics of collagen fibers (CF). CF is a natural biomacromolecule owning an ordered one-dimensional (1D) hierarchical fibrous structure with abundant active functional groups, which endow it with high reactivity of binding to multivalent Ti4+ and Ce4+ and also make it an ideal structural template to direct the formation of TCBs through a simple thermal pyrolysis. The results demonstrate that use of the 1D hierarchically structured CF as the template is able to impede the phase transformation of the resultant TiO2 nanofiber bundles from anatase to rutile when calcinated at 600 degrees C, while the introduction of ultrafine CeO2 nanocrystals into the TCBs can further inhibit the growth of the TiO2 crystal grains as well as their phase transformation even at a higher calcination temperature of 700 degrees C. Such a synergistic effect stemming from the CF template and CeO2 nanocrystals not only favors the formation of high-temperature stable anatase TiO2 nanofiber bundles, but also allows them to possess faster ionic diffusion, larger specific surface area for electrochemical reaction, and pseudocapacitance-boosted charge storage capability. As a result, the as-built TCBs are evaluated as the anode materials, which exhibit excellent electrochemical lithium storage properties in terms of high specific capacity (393 mAh g(-1) at 20 mA g(-1)), good rate capability (75 mAh g(-1) at 1600 mA g(-1)), and long cycling life (almost 100% capacity retention after 1200 cycles).