Blue Emitting CsPbBr3: High Quantum Confinement Effect and Well‐Adjusted Shapes (Nanorods, Nanoplates, and Cubes) toward White Light Emitting Diodes
Wenbin Shi,Xiao Zhang,Cong Xie,Hsueh Shih Chen,Ping Yang
DOI: https://doi.org/10.1002/adom.202302129
IF: 9
2023-11-04
Advanced Optical Materials
Abstract:Blue emitting CsPbBr3 nanocrystals with various morphologies (e.g. nanorods (NRs), nanoplates (NPLs), and cubes) are prepared by controlling the nucleation and growth. The NRs and NPLs reveal narrow photoluminescence (PL) spectra and high PL efficiencies of 74% and 60%, respectively. Similar procedures are used to create CsPbI3 NRs and NPLs. A white light emitting diode will show the broad applications. Controlled nucleation and slow growth endow blue emitting CsPbX3 nanocrystals (NCs) with bright photoluminescence (PL), which is crucial needed in luminescent devices. In this paper, a low‐temperature injection synthesis method is developed to control nucleation and the growth process by decreasing the reaction rate of ions, thereby controlling the morphologies of CsPbX3 NCs in clusters, nanorods (NRs), nanoplates (NPLs), and nanocubes by adjusting precursors, ligands, and injection parameters. CsPbX3 NCs exhibit excellent PL properties such as high quantum confinement effect. The PL peak wavelengths of CsPbBr3 NPLs and NRs are at 451 and 467 nm, respectively, in which their full width at half maximum (FWHM) of PL spectra is 22 and 12 nm, while their PL efficiencies are 65 and 74%, respectively. The method is further used to create CsPbI3 and CsPbCl3. CsPbI3 NPLs and NRs reveal PL peaks at 590 and 600 nm and PL efficiencies of 56% and 60%, respectively. These NCs exhibit excellent stability against ultraviolet light irradiation. A color conversion layer for white light‐emitting diodes is fabricated using these highly bright NCs. A Commission Internationale d'Eclairage color coordinate of (0.31,0.33) is located at the white light region specified by Rec.2020 standard, and the color temperature reaches 6189 K.
materials science, multidisciplinary,optics