Abstract:TiO2-diatomite photocatalysts were prepared by sol-gel process with various pre-modified diatomite. In order to obtain diatomite with different surface characteristics, two modification approaches including calcination and phosphoric acid treatment on the micro-structure of diatomite are introduced. The photocatalysts were characterized by XRD, XPS, nitrogen adsorption-desorption isotherms and micromorphology analysis. The results indicate that, compared with pure TiO2, the anatase-to-rutile phase transition temperature of TiO2 loaded on diatomite carrier is significantly increased to nearly 900 degrees C, depending on the different pretreatment method of diatomite. The photocatalytic activities of different samples were evaluated by their degradation rate of methyl orange ( MO) dye under UV and visible-light irradiation. The samples prepared by phosphoric acid pretreatment method exhibit the highest photocatalytic activity. After 90 min of UV irradiation, about 90% of MO is decomposed by the best effective photocatalyst. And after 8 h visible-light irradiation, nearly 60% of MO is decomposed by the same sample. Further mechanism investigation reveals that the H3PO4 pretreatment process can obviously change the surface features of diatomite carrier, cause the formation of Si-O-Ti bond, increase the binding strength between TiO2 and diatomite, restrain crystal growth of loaded TiO2, and thus form thermal-stable meso-porous structure at the granular spaces. It helps to build micro-, meso- and macro-porous hierarchical porous structure in TiO2-diatomite, and improves the charge and mass transfer efficiency during catalyzing process, resulting in the significantly increased photocatalytic activity of TiO2-diatomite pretreated by phosphoric acid. (C) 2014 Elsevier B. V. All rights reserved.

Preparation and Characterisation of Ag Modified Rutile Titanium Dioxide and Its Photocatalytic Activity under Simulated Solar Light

Preparation of WO<sub>x</sub>-TiO<sub>2</sub> and the Photocatalytic Activity under Visible Irradiation

Influence of Preparation Method on Morphology and Photocatalysis Activity of Nanostructured TiO2.

Preparation of AgI Sensitized Amorphous TiO2 As Novel High-Performance Photocatalyst for Environmental Applications

Interface Actions Between TiO2 and Porous Diatomite on the Structure and Photocatalytic Activity of TiO2-diatomite

Characterization and Improved Solar Light Activity of Vanadium Doped TiO2/diatomite Hybrid Catalysts

Preparation and activity of Ag-TiO2 photocatalyst with multi-valency state

Ag-SrTiO3/TiO2 Composite Nanostructures with Enhanced Photocatalytic Activity

Synthesis and Properties of Nano-Rutile Tio2 Photocatalysts

Preparation of Er3+:YAlO3/Fe-doped TiO2–ZnO and its application in photocatalytic degradation of dyes under solar light irradiation

One-Step Synthesis Of Bifunctional Tio2 Catalysts And Their Photocatalytic Activity

Preparation and Characterization of Silica-modified Titanium Dioxide Nanoparticles by Co-precipitation Method

Highly Active Rutile TiO 2 for Photocatalysis

Tunable Synthesis of Enhanced Photodegradation Activity of Brookite/Anatase Mixed-Phase Titanium Dioxide

Synthesis, Characterization, and Photocatalytic Properties of Ag Modified Hollow SiO2/TiO2 Hybrid Microspheres

Size-dependent Surface Activity of Rutile and Anatase TiO2 Nanocrystals: Facile Surface Modification and Enhanced Photocatalytic Performance.

Controllable Synthesis and Tunable Photocatalytic Properties of Ti3+-doped TiO2

Anatase-TiO2 nano-particle preparation with a micro-mixing technique and its photocatalytic performance

Improved photocatalytic activity of rutile TiO2 for organic oxidation through Ag nanoparticles and borate anions

Checking the Synergetic Effect Between Anatase and Rutile

Evaluating Intrinsic Photocatalytic Activities of Anatase and Rutile TiO2 for Organic Degradation in Water