Abstract:In this study, to solve the problem of reduced efficiency of NO degradation due to the agglomeration effect of TiO2 nanoparticles, nano-TiO2 was converted to a 3D-ordered microporous [three-dimensional ordered macroporous (3DOM)] structure and combined with fog seal technology, which is expected to improve the degradation performance of nano-TiO2 on NO gas in automobile exhaust. We optimized the preparation process parameters of 3D-ordered macroporous (3DOM) TiO2 and developed and designed an experimental device for exhaust-gas catalytic degradation. We further tested and analyzed the effects of emulsified asphalt type, photocatalyst type, doping amount, and 3DOM TiO2 pore size on the photocatalytic performance of 3DOM TiO2 fog seal material. The effects of 3DOM TiO2 fog seal material on road antiskid performance were evaluated herein. The results show that the optimal coating volume of the PS microsphere solution is 0.14−0.16 mL/cm2. The optimal filling time of the precursor solution is 20 min for the preparation of 3DOM TiO2 materials by the sandwich method. The degradation efficiency of 3DOM TiO2 fog seal material for the optimal pore size was 17.0%, 15.0%, and 25.1% higher than that of nano-TiO2, respectively. The 3D-ordered pore structure reduces the agglomeration effect of nano-TiO2 Thus, the degradation efficiency is improved. With the increase of 3DOM TiO2 doping, the degradation efficiency of fog seal materials gradually increased. However, the increment of degradation efficiency decreased. The appropriate increase of 3DOM TiO2 pore size is beneficial to the catalytic effect of light. If the pore size is significantly large, the emulsified asphalt will block the pore space and reduce the contact area between 3DOM TiO2 and exhaust gas. The optimal pore size is 300 nm. The type of emulsified asphalt on 3DOM TiO2 fog seal material degradation effect is not significant. The antislip performance of the pavement coated with 3DOM TiO2 fog seal materials can meet the requirements of specifications. The photocatalyst doping amount, type, and different 3DOM TiO2 pore sizes do not significantly affect the antislip performance of the fog seal. The novel 3DOM TiO2 photocatalytic pavement material proposed in this study is of positive significance for the reduction of automobile exhaust pollution.

Decomposition of Vehicle Exhaust on Pavement with Nanotitanium Oxide and Promoting Function of Pyroelectric Materials

Research on the Efficiency of Decomposition of Hydrocarbon in Exhaust gas from Vehicles by Nanometer Titanium dioxide

Photocatalytic Degradation of Vehicular Exhaust by Nitrogen-Doped Titanium Dioxide Modified Pavement Material

Application of Nanometer Titanium Dioxide in Vehicle Exhaust Decomposing

Application of Photocatalytic Concrete Paint and Its Effect of Decomposing Vehicle Exhaust

Application of Nano- TiO2 Used in Road Engineering and its Long-Term Decomposition Effect

Pollution Control of NOx on Asphalt Pavement in the Forest Region Highway

Automobile Exhaust Removal Performance of Pervious Concrete with Nano TiO2 under Photocatalysis.

Photocatalytic Degradation of Vehicle Exhausts on Asphalt Pavement by Tio2/Rubber Composite Structure

Vehicle Exhaust Gas Clearance By Low Temperature Plasma-Driven Nano-Titanium Dioxide Film Prepared By Radiofrequency Magnetron Sputtering

Preparation, characterization and photocatalytic degradation efficacy of bismuth oxide under visible and ultraviolet light

Low temperature plasma-driven catalysis of nanotitanium dioxide for vehicle exhaust clearance

An Analysis on the Microstructure and Oxidation Characteristics of Particles from Diesel Engine in Exhaust Gas Transport Process

The Application of Nanometer Titanium Dioxide in Road Engineering

Application Performance Evaluation on Material of Automobile Exhaust Degradation in Asphalt Pavement

Regulation of Electron Density in Pt Nanoparticles Via Bimetallic Metal-Organic Frameworks for Enhancing Photothermal Catalysis of Toluene Decomposition

Photocatalytic Degradation of Vehicle Exhaust by Nano-TiO2 Cement Slurry: Experimental Factors and Field Application

PHOTOCATALYTIC OXIDATION OF NITROGEN OXIDES BY NANO-TiO2 IMMOBILIZED ON ROAD SURFACE MATERIALS

The Technology of Degradation Car Tail Gas Through the Method of Nano-TiO2 Immobilized on the Semi-flexible Pavement

Evaluation of Nano-TiO2 Modified Waterborne Epoxy Resin As Fog Seal and Exhaust Degradation Material in Asphalt Pavement

Performance Study of 3DOM TiO2 Fog Seal Material for Photocatalytic Degradation of NO in Vehicle Exhaust