Performance Study of 3DOM TiO2 Fog Seal Material for Photocatalytic Degradation of NO in Vehicle Exhaust
Ying Xu,Xinzhou Li,Moxuan Duan,Zhongqi Fan,Zihan Wang,Shifa Xu,Hao Liu
DOI: https://doi.org/10.1061/jmcee7.mteng-15843
IF: 3.2
2023-12-01
Journal of Materials in Civil Engineering
Abstract:In this study, to solve the problem of reduced efficiency of NO degradation due to the agglomeration effect of TiO2 nanoparticles, nano-TiO2 was converted to a 3D-ordered microporous [three-dimensional ordered macroporous (3DOM)] structure and combined with fog seal technology, which is expected to improve the degradation performance of nano-TiO2 on NO gas in automobile exhaust. We optimized the preparation process parameters of 3D-ordered macroporous (3DOM) TiO2 and developed and designed an experimental device for exhaust-gas catalytic degradation. We further tested and analyzed the effects of emulsified asphalt type, photocatalyst type, doping amount, and 3DOM TiO2 pore size on the photocatalytic performance of 3DOM TiO2 fog seal material. The effects of 3DOM TiO2 fog seal material on road antiskid performance were evaluated herein. The results show that the optimal coating volume of the PS microsphere solution is 0.14−0.16 mL/cm2. The optimal filling time of the precursor solution is 20 min for the preparation of 3DOM TiO2 materials by the sandwich method. The degradation efficiency of 3DOM TiO2 fog seal material for the optimal pore size was 17.0%, 15.0%, and 25.1% higher than that of nano-TiO2, respectively. The 3D-ordered pore structure reduces the agglomeration effect of nano-TiO2 Thus, the degradation efficiency is improved. With the increase of 3DOM TiO2 doping, the degradation efficiency of fog seal materials gradually increased. However, the increment of degradation efficiency decreased. The appropriate increase of 3DOM TiO2 pore size is beneficial to the catalytic effect of light. If the pore size is significantly large, the emulsified asphalt will block the pore space and reduce the contact area between 3DOM TiO2 and exhaust gas. The optimal pore size is 300 nm. The type of emulsified asphalt on 3DOM TiO2 fog seal material degradation effect is not significant. The antislip performance of the pavement coated with 3DOM TiO2 fog seal materials can meet the requirements of specifications. The photocatalyst doping amount, type, and different 3DOM TiO2 pore sizes do not significantly affect the antislip performance of the fog seal. The novel 3DOM TiO2 photocatalytic pavement material proposed in this study is of positive significance for the reduction of automobile exhaust pollution.
construction & building technology,materials science, multidisciplinary,engineering, civil