Abstract:In this study, a high-performance Mg–8Gd–2Y–1Zn–6Li (wt%) alloy having a TYS of 202 ± 2.6 MPa, UTS of 243 ± 2.1 MPa and EL of 10.7 ± 2.3% was successfully fabricated by casting, heat treatment and hot extrusion. The effects of intermetallic compounds on microstructure and mechanical properties were deeply investigated. The results show that the studied alloy consists of coarse deformed α-Mg grains with (0001) basal texture, fine recrystallized β-Li grains with (002) texture and three Mg3RE phase variants, which are bulk Mg3RE phase with a size range of 10–30 µm, spot Mg3RE phase with a size range of 1–2 µm and spherical Mg3RE phase with a size range of 0.3–1 µm, respectively. The spherical Mg3RE phase has a strong dispersion strengthening effect, while the bulk Mg3RE phase acts as crack resources and deteriorates the ductility. A novel island-like <math>β1R</math> phase (FCC, a = 0.78 nm) is found for the first time in the Mg-Gd-Li based alloys. It has a coherent <math>(1̅12)β1R</math>//<math>(101̅0)α</math> interface at the broad facet and a semi-coherent <math>(1̅11)β1R</math>//<math>(112̅0)α</math> interface at the end facet. The <math>β1R</math> phase transforms from <math>βH</math> phase at the semi-coherent interface by atomic shear of RE and Mg atoms. The <math>β1R</math> phase provides a significant precipitation strengthening effect to the studied alloy, while the dissolution of <math>β1R</math> phase results in the age-softening phenomenon. The high-performance of the studied alloy is mainly attributed to the α/β duplex structure, three Mg3RE phase variants, and <math>β1R</math> phase.

Microstructure and Mechanical Properties of Hot Extruded Mg-8.89Li-0.96Zn Alloy

Microstructure Evolution and Properties of Mg-9Gd-0.8Al Alloy with Lamellar Phase During Extrusion at Different Temperatures

Numerical and Experimental Investigation on Hot Backward Extrusion Process of Mg-Gd-Y-Zn-Zr Magnesium Alloy

Microstructure and mechanical properties of Mg-Gd-Zn-Zr alloy after hot extrusion

Effect of Hot Extrusion on Microstructure, Texture, and Mechanical Properties of Mg-Zn-Mn-0.5Ca Alloy

Investigation on corrosion behavior and mechanical properties of an extruded Mg-Zn-Al-Sn-Mn alloy

Hot Extrusion Effect on the Microstructure and Mechanical Properties of a Mg–Y–Nd–Zr Alloy

Microstructure and Mechanical Properties of Extruded Mg-Zn-Nd-Y-Zr-Ca Alloy

Microstructure, Non-Basal Texture and Strength-Ductility of Extruded Mg-6Bi-3Zn Alloy

Microstructures and mechanical properties of as-extruded Mg–8Gd–2Y–1Zn–6Li alloy

Effect of extrusion temperature on microstructure, mechanical properties, and deformation mechanism of Mg-2.5Er-0.6Zr alloy

Optimization of Microstructure and Mechanical Property of a Mg-Zn-Y-Nd Alloy by Extrusion Process

Microstructures and Mechanical Properties of a High-Strength Mg-3.5Sm-0.6Zn-0.5Zr Alloy

Effects of extrusion ratio and temperature on the microstructure and mechanical properties of Mg–Zn–Yb–Zr extrusion alloys

Microstructure evolution, strengthening mechanisms and deformation behavior of high-ductility Mg−3Zn−1Y−1Mn alloy at different extrusion temperatures

Microstructure evolution difference in Mg96.5Gd2.5Zn1 alloys extruded from as-cast and solution-treated states

Microstructure and mechanical properties of a low-alloyed Mg-Zn-Al-Ca alloy: Effect of extrusion speed

Revealing the dynamic recrystallization mechanism, extrusion deformation mechanism, and tensile deformation behavior of Mg–6Al–1Zn–1.1Sc alloy

Influence of Extrusion Ratio on Microstructure and Tensile Properties of Mg–Gd–Y–Zn–Zr Alloy

Effect of Extrusion Process on Microstructure, Corrosion Properties, and Mechanical Properties of Micro-Alloyed Mg–Zn–Ca–Zr Alloy

Microstructures, hot tensile deformation behavior and constitutive modeling in a superlight Mg-2.76Li-3Al-2.6Zn-0.39Y alloy