Laser Butt Welding of 6.6Mm-Thick D406A Ultra-High-Strength Steel: Part II—Bending Deformation Ability of Joints
Miaoxia Xie,Zongyang Lv,Jun Wu,Lixu Zhang,Han Yu,Jian Long,Linjie Zhang
DOI: https://doi.org/10.1007/s11665-024-09905-6
IF: 2.3
2024-01-01
Journal of Materials Engineering and Performance
Abstract:To address the insufficient bending deformation ability of laser-welded joints of D406A ultra-high-strength steel, the microstructures and mechanical performance of laser-welded joints (Joint-HT1 and Joint-HT2) of D406A steel prepared using two heat treatment (HT) processes were compared. One HT(heat treatment) process was combination of quenching and medium-temperature tempering, heated from the room temperature to 930 °C at 10 K/min, followed by 85 min of holding, oil quenching, heating to 300 °C in a furnace, holding for 180 min, and finally air-cooling to the room temperature (HT1), and the other was combination of high-temperature tempering, quenching, and medium-temperature tempering, heated at 10 K/min from the room temperature to 650 °C and held for 85 min, heated again to 930 °C and held for 68 min, oil-quenched, heated to 300 °C and held for 180 min, and air-cooled to the room temperature (HT2). The results show that the microstructures in the weld of Joint-HT1 mainly include tempered martensite, whereas the weld of Joint-HT2 not only contains tempered martensite but also martensite-austenite islands. Alteration of the microstructure gives rise to variations in the mechanical properties. The cross-sections of the two joints exhibited uniform microhardness, and the microhardness of the section of Joint-HT2 was approximately 140 HV lower than that of Joint-HT1 overall. Moreover, the front and back sides of Joint-HT2 were probably decarburized, whereas no decarburization was found on Joint-HT1. The average tensile strength and elongation of Joint-HT1 were 1746 MPa and 3.5