A Laser-Induced TIG Arc Narrow-Gap Welding Technique for TC4 Titanium Alloy Thick Plates Based on the Spatial Position Control of Laser, Arc and Filler Wire

Gang Song,Zhijie Xu,Qiang Lang,Xin Liu,Hongyang Wang,Liming Liu

DOI: https://doi.org/10.3390/met14050510

IF: 2.695

2024-04-27

Metals

Abstract:In this paper, a novel laser-induced TIG arc narrow-gap welding technology is proposed for thick plates of TC4 titanium alloy. The feasibility of achieving high-performance welding joints is investigated by adjusting the spatial deviation position of the laser, arc, and filler wire. The results exhibited remarkable capabilities. By augmenting the laser-arc malposition, a stable deflection of the arc can be achieved, resulting in enhanced heat input to the sidewall adjacent to the laser side and improved fusion capability. Moreover, an inclined weld can be obtained through increased malposition between the filler wire and arc, which helps to improve interlayer fusion and suppress porosity defects. This method, involving alternating bilateral offsets between passes, successfully achieved narrow-gap welding of 24 mm-thick TC4 titanium alloy with an average tensile strength of 880.68 MPa (equivalent to 95.05% of base material strength). Therefore, this technology exhibits promising potential as an automated welding technique for achieving high-quality narrow-gap welding in titanium alloys.

materials science, multidisciplinary,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The paper primarily explores a novel laser-induced TIG arc narrow gap welding technology, aiming to address the high-quality welding issues of TC4 titanium alloy thick plates. Specifically, the paper addresses the following key issues:

1. **Improving Welding Quality**: By adjusting the spatial position deviation (i.e., offset) of the laser, arc, and filler wire, the quality of the welding joint is improved. The study found that increasing the offset between the laser and the arc can achieve stable deflection of the arc, thereby increasing the heat input near the laser sidewall and improving fusion capability.

2. **Controlling Interlayer Fusion and Suppressing Porosity Defects**: By increasing the offset between the filler wire and the arc, an inclined weld seam can be obtained, which helps improve interlayer fusion and suppress the generation of porosity defects.

3. **Achieving Automated Welding**: Using the aforementioned methods, successful narrow gap welding of 24 mm thick TC4 titanium alloy plates was achieved, with an average tensile strength of 880.68 MPa (equivalent to 95.05% of the base material strength). This indicates that the technology has the potential to be used as an automated welding technology for achieving high-quality narrow gap welding of titanium alloys.

In summary, the main objective of the paper is to develop a new technology that can effectively solve common problems in the welding of thick titanium alloy plates, including improving fusion performance, enhancing interlayer fusion, and reducing defects such as porosity, ultimately achieving efficient and high-quality welding results.