Abstract:PANI/FeS2/MnO2 composite electrode materials were successfully prepared. The results showed that the specific capacitance of PANI/FeS2/MnO2 4 : 1 : 3 was 580 F/g at 1 A/g, and the capacitance retention rate was 85.2 % after cycling 10,000 times at 5 A/g. The asymmetric supercapacitor PANI/FeS2/MnO2 4 : 1 : 3 //AC had an energy density of 37.93 Wh/kg at a power density of 0.85 kW/kg. Polyaniline (PANI) has unique physical and chemical peculiarities, so it has been widely researched in the field of energy storage. However, its structure is easy to be damaged during charging and discharging, which seriously affects its application. PANI/FeS2/MnO2 composite materials were successfully prepared by an easy combination of chemical precipitation and chemical oxidative polymerization. The electrochemical test results manifested that the specific capacitance of PANI/FeS2/MnO2 4 : 1 : 3 was 580 F/g at 1 A/g, and had great cyclic stability (capacitance retention rate was 85.2 % after 10000 cycles at 5 A/g). It was because that reticular structure shortened the ion transport path. On the other hand, it was able to effectively mitigate the volume change during long‐term charging and discharging, thus improving the cycling stability. In addition, PANI/FeS2/MnO2 4 : 1 : 3 as the positive and activated carbon (AC) as the negative, an asymmetrical supercapacitor was assembled with a maximal energy density of 37.93 Wh/kg when its power density was 0.85 kW/kg. At the same time, the device possessed a long cycle life (the capacitance conservation rate was 82 % after 5000 cycles at 5 A/g). This excellent performance is due to the excellent synergy between the PANI, FeS2 and MnO2. This study opens a new way to investigate polyaniline‐based composite electrode materials.

Synergistically Reinforced Capacitive Performance from a Hierarchically Structured Composite of Polyaniline and Cellulose-Derived Highly Porous Carbons

Polyaniline coated 3D crosslinked carbon nanosheets for high-energy-density supercapacitors

Hybrids of Highly Ordered Polyaniline/Carbon Fibers for High-Performance Supercapacitor Electrodes

3D Hybrids of Interconnected Porous Carbon Nanosheets/Vertically Aligned Polyaniline Nanowires for High‐Performance Supercapacitors

Biomass-Based Porous N-Self-Doped Carbon Framework/Polyaniline Composite with Outstanding Supercapacitance

Hierarchical Co3O4/PANI Hollow Nanocages: Synthesis and Application for Electrode Materials of Supercapacitors

Construction of tunable ZnCoO x /C-PANI electrode materials for high-performance supercapacitors

Improved electrochemical performance of hierarchical porous carbon/polyaniline composites

High-performance electrochemical supercapacitors based on polyoxometalate integrated into polyaniline and activated carbon nanohybrid

Boosting the Utilization and Electrochemical Performances of Polyaniline by Forming a Binder-Free Nanoscale Coaxially Coated Polyaniline/Carbon Nanotube/Carbon Fiber Paper Hierarchical 3D Microstructure Composite as a Supercapacitor Electrode

TiO2-C Nanowire Arrays@polyaniline Core-Shell Nanostructures on Carbon Cloth for High Performance Supercapacitors

Biomass-derived N, S co-doped activated carbon-polyaniline nanorod composite electrodes for high-performance supercapacitors

Enhanced Electrochemical Performance of a Hybrid Supercapacitive Material Based on Ternary Doped Polyaniline/Activated Carbon Composite

Hierarchical PANI/NiCo-LDH Core-Shell Composite Networks on Carbon Cloth for High Performance Asymmetric Supercapacitor

Freestanding Hierarchically Porous Carbon Framework Decorated by Polyaniline As Binder-Free Electrodes for High Performance Supercapacitors

Development of PANI/FeS2/MnO2 Composite Electrode Materials for High‐Performance Supercapacitors

Facile Synthesis of a Ni-based NiCo2O4-PANI Composite for Ultrahigh Specific Capacitance

Construction of hierarchical graphene/polyaniline@polyaniline electrodes by chemical and electrochemical polymerization for high-energy supercapacitors

Lamellar Hierarchical Lignin-Derived Porous Carbon Activating the Capacitive Property of Polyaniline for High-Performance Supercapacitors.

A Novel Polyaniline Nanowire Arrays/Three‐Dimensional Graphene Composite for Supercapacitor

Synergistic Capacitive Behavior Between Polyaniline and Carbon Black