Abstract:PANI/FeS2/MnO2 composite electrode materials were successfully prepared. The results showed that the specific capacitance of PANI/FeS2/MnO2 4 : 1 : 3 was 580 F/g at 1 A/g, and the capacitance retention rate was 85.2 % after cycling 10,000 times at 5 A/g. The asymmetric supercapacitor PANI/FeS2/MnO2 4 : 1 : 3 //AC had an energy density of 37.93 Wh/kg at a power density of 0.85 kW/kg. Polyaniline (PANI) has unique physical and chemical peculiarities, so it has been widely researched in the field of energy storage. However, its structure is easy to be damaged during charging and discharging, which seriously affects its application. PANI/FeS2/MnO2 composite materials were successfully prepared by an easy combination of chemical precipitation and chemical oxidative polymerization. The electrochemical test results manifested that the specific capacitance of PANI/FeS2/MnO2 4 : 1 : 3 was 580 F/g at 1 A/g, and had great cyclic stability (capacitance retention rate was 85.2 % after 10000 cycles at 5 A/g). It was because that reticular structure shortened the ion transport path. On the other hand, it was able to effectively mitigate the volume change during long‐term charging and discharging, thus improving the cycling stability. In addition, PANI/FeS2/MnO2 4 : 1 : 3 as the positive and activated carbon (AC) as the negative, an asymmetrical supercapacitor was assembled with a maximal energy density of 37.93 Wh/kg when its power density was 0.85 kW/kg. At the same time, the device possessed a long cycle life (the capacitance conservation rate was 82 % after 5000 cycles at 5 A/g). This excellent performance is due to the excellent synergy between the PANI, FeS2 and MnO2. This study opens a new way to investigate polyaniline‐based composite electrode materials.

Biomass-Based Porous N-Self-Doped Carbon Framework/Polyaniline Composite with Outstanding Supercapacitance

Freestanding Hierarchically Porous Carbon Framework Decorated by Polyaniline As Binder-Free Electrodes for High Performance Supercapacitors

Fabrication of 3D Lawn-Shaped N-doped Porous Carbon Matrix/polyaniline Nanocomposite As the Electrode Material for Supercapacitors

Construction of Ultrathin Nitrogen-Doped Porous Carbon Nanospheres Coated With Polyaniline Nanorods for Asymmetric Supercapacitors

Biomass-derived N, S co-doped activated carbon-polyaniline nanorod composite electrodes for high-performance supercapacitors

Boosting the Utilization and Electrochemical Performances of Polyaniline by Forming a Binder-Free Nanoscale Coaxially Coated Polyaniline/Carbon Nanotube/Carbon Fiber Paper Hierarchical 3D Microstructure Composite as a Supercapacitor Electrode

Development of PANI/FeS2/MnO2 Composite Electrode Materials for High‐Performance Supercapacitors

A Novel Polyaniline Nanowire Arrays/Three‐Dimensional Graphene Composite for Supercapacitor

All-organic Covalent Organic Framework/polyaniline Composites As Stable Electrode for High-Performance Supercapacitors

Three-dimensional Cross-Linked Polyaniline Fiber/n-Doped Porous Carbon with Enhanced Electrochemical Performance for High-Performance Supercapacitor

A Novel Sustainable Flour Derived Hierarchical Nitrogen-Doped Porous Carbon/Polyaniline Electrode for Advanced Asymmetric Supercapacitors

Vapor deposition polymerization of aniline on 3D hierarchical porous carbon with enhanced cycling stability as supercapacitor electrode

Synthesis of wood derived nitrogen-doped porous carbon–polyaniline composites for supercapacitor electrode materials

NiCo2O4@Polyaniline Nanotubes Heterostructure Anchored on Carbon Textiles with Enhanced Electrochemical Performance for Supercapacitor Application

Polyaniline Coated Boron Doped Biomass Derived Porous Carbon Composites for Supercapacitor Electrode Materials

Lignin-based composites for high-performance supercapacitor electrode materials

Polyaniline-modified Porous Carbon Tube Bundles Composite for High-Performance Asymmetric Supercapacitors

Vertically Aligned Polyaniline Nano-Array Decorated on Ultra-Thin MXene Nanosheets for High Energy Density Supercapacitors

Facile Synthesis of a Ni-based NiCo2O4-PANI Composite for Ultrahigh Specific Capacitance

In-situ Electropolymerization of Porous Conducting Polyaniline Fibrous Network for Solid-State Supercapacitor

Facile Synthesis of Nitrogen-Doped Porous Carbon As Robust Electrode for Supercapacitors