Abstract:The oxidation of bond coat (BC) and interdiffusion between BC layer and superalloys were two mechanisms that contribute to the degradation of thermal barrier coating system (TBCs). The oxidation and interdiffusion of TBCs on single-crystal superalloys were comparatively studied in this work at 950 °C, 1050 °C and 1100 °C over a duration of 1500 h. The results indicated that the thickness of the thermally grown oxide (TGO) progressively increased with the oxidation time and temperature, following a parabolic law. The discontinuous TGO gradually developed into a double-layer structure: the upper layer was a mixed oxide layer, while the lower layer predominantly comprises an Al 2 O 3 layer. Moreover, an interdiffusion zone (IDZ) is formed at the interface between the BC layer and the substrate, with its thickness increasing in response to both temperature and oxidation time. The Cr-rich phases appeared in the IDZ, where Al initially diffused from the BC layer to the substrate, followed by a reverse diffusion process. Simultaneously, Ni and refractory elements diffused from the substrate into IDZ, resulting in the precipitation of the topologically close-packed (TCP) phases and the formation of a secondary reaction zone (SRZ). It has further been shown that Cr-rich phases further diffused into SRZ. Higher oxidation temperatures accelerated the growth of the SRZ and facilitated the transformation of the TCP phases from a blocky to a needle-like morphology. Ultimately, the continuous growth of IDZ and SRZ led to the evolution of the substrate from a monocrystalline to a polycrystalline structure. This study provides valuable data on the microstructural evolution of TBCs and the assessment of their service life.

Interdiffusion Behavior and Lifetime Prediction of Co-Al Coating on Ni-based Superalloy

Effect of Substrate Characteristics on Interdiffusion Coefficients of Ni and Al Atoms in Β-Nial Phase of Aluminide Coatings

Influences of MCrAlY Coatings and TBCs on Oxidation Behavior of a Ni-Based Single Crystal Superalloy

On the Oxidation and Interdiffusion Behavior of an AlCoCrFeNiY High-Entropy Alloy Bond Coat on a Directionally Solidified Ni-based Superalloy

Interdiffusion Behavior and Compositional Tailoring of AlCoCrFeNiY High-Entropy Alloy Coating on a Hastelloy-X Superalloy

The Interdiffusion Behavior of NiCoCrAlYHf Coating Deposited by Arc Ion Plating on Carburized Ni-Based Single Crystal Superalloy

Aluminide Coating Prepared on Ni-Base Superalloy by Pack Cementation

Effects of aluminised-coating on microstructure and properties of Ni–Co-base superalloys

Interdiffusion mechanism at the interface between TiAl alloy and NiCoCrAlY bond coating

High temperature oxidation and interdiffusion behavior of recoated NiCoCrAlY coating on a nickel-based superalloy

Microstructural evolution of NiCoCrAlY coated directionally solidified superalloy

Comparative study of temperature-dependent oxidation and interdiffusion behavior on NiCoCrAlYHf-coated nickel-based single-crystal superalloys

Tuning the secondary reaction zone between PtAl coating and nickel based single crystal superalloy during high-temperature oxidation through regulating aluminizing time

Microstructure evolution and interdiffusion behaviors of (Ni,Pt)Al coating with and without Re-diffusion barrier on IC21 substrate at 1100°C

Microstructural evolution and element interdiffusion of NiAlHf and NiAlHfY coatings deposited on a Ni-based superalloy

Tailoring coating composition for the associated microstructural stability of a single-crystal superalloy: an experimental and simulation study

Understanding the Oxidation Behaviors of a Ni-Co-based Superalloy at Elevated Temperatures Through Multiscale Characterization

Structure and High-Temperature Oxidation Performance of Si-Co Diffusion Coatings Prepared on a TiAl-Nb Alloy

A Magnetron Sputtered Microcrystalline Β-Nial Coating for SC Superalloys. Part II. Effects of a NiCrO Diffusion Barrier on Oxidation Behavior at 1100 °C

Oxidation Behavior of Aluminide Coatings on Cobalt-Based Superalloys by a Vapor Phase Aluminizing Process

Temperature-dependent evolution mechanism of interface microstructure between gradient MCrAlY coatings and nickel-based superalloy