Abstract:Spent selective catalytic reduction (SCR) catalysts are environmentally hazardous and resource-enriching. In this work, V, W, and As in a spent SCR catalyst was extracted by alkali pressure leaching . Results showed that the V, W, and As were loaded on the anatase TiO 2 crystal grains as amorphous oxides . The optimum pressure leaching conditions were NaOH concentration of 20 wt%, reaction temperature of 180 °C, reaction time of 120 min, L/S of 10 mL/g, and stirring speed of 300 rpm. The leaching efficiency of W, V, and As reached 98.83%, 100%, and 100%, respectively. The experiment revealed the preferential leaching of V and As rather than W, and the leaching mechanisms of V, W, and As were studied through experiment and density functional theory (DFT). The leaching kinetics of W conformed to a variant of the shrinking core model and the leaching process of W is controlled by both chemical reactions and diffusion processes. During the leaching process, Na 2 Ti 2 O 4 (OH) 2 product powder layer was generated, which affects the mass transfer of W. The destruction of the TiO 2 skeleton in the spent SCR catalyst is essential for adequate W extraction, especially for the extraction of W embedded in the TiO 2 lattice. The DFT simulation result indicated that the V and As loaded onto the TiO 2 support are easier to absorb hydroxide ions rather than W, and the leaching reaction energy of V and As was lower than W, As, and V has leaching priority over the leaching of W. Furthermore, an anatase TiO 2 photocatalyst with the {001} crystal surface exposed was successfully prepared from the alkali pressure leaching residue. This work provides theoretical support for the metal leaching and utilization of spent SCR catalysts via alkali pressure leaching.

Leaching Behavior of Vanadium from Spent SCR Catalyst and Its Immobilization in Cement-Based Solidification/stabilization with Sulfurizing Agent

Tuning of vanadium valence for value-added recycling and utilization of vanadium from spent Selective Catalytic Reduction Catalysts

Leaching Vanadium from the Spent Denitration Catalyst in the Sulfuric Acid/Oxalic Acid Combined Solvent

Melting Solidification and Leaching Behaviors of V/As During Co-Combustion of the Spent SCR Catalyst with Coal

Solidification and Leaching Behaviors of V and As in a Spent Catalyst-Containing Concrete

A clean and efficient approach for recovery of vanadium and tungsten from spent SCR catalyst

A promising method to recover spent V2O5–WO3/TiO2 catalyst: treatment by vanadium–titanium magnetite sintering process

Vanadium Recovery from Spent SCR Denitration Catalyst by Reductive Acid Leaching and Ammonium Precipitation

Selective leaching of V, W and recycling of TiO2 carrier from waste V2O5-WO3/TiO2 catalysts by mixed alkali liquor

Extraction and Separation of Tungsten and Vanadium from Spent V2O5-WO3/TiO2 SCR Catalysts and Recovery of TiO2 and Sodium Titanate Nanorods as Adsorbent for Heavy Metal Ions

Cement and zeolite stabilization/solidification of heavy metal-contaminated sediments: 841-Day leaching characteristics, mechanisms, and microstructure

Studies on Recovery of Vanadium from Desilication Residue Obtained from Processing of a Spent Catalyst

Extraction of W, V, and As from spent SCR catalyst by alkali pressure leaching and the pressure leaching mechanism

Speciation Analysis and Leaching Behaviors of Selected Trace Elements in Spent SCR Catalyst

Ultrasound assisted enhancement in vanadium and tungsten leaching from waste SCR catalyst

Method for separating vanadium and tungsten leachate from failed SCR (selective catalytic reduction) denitration catalyst

A Promising Approach to Recover a Spent SCR Catalyst: Deactivation by Arsenic and Alkaline Metals and Catalyst Regeneration

Recovery of vanadium and tungsten from spent selective catalytic reduction catalyst by alkaline pressure leaching

Solidification of Radioactive Spent Liquid Scintillator Wastes: Effect of Additives on the Leaching of Radionuclides

Effects of Urea and Sodium Tripolyphosphate on the Hydration and Leaching of Cr(VI) in Solid Waste–Based Sulfoaluminate Cement

Environmentally-friendly Harvesting TiO2 Nanospheres and V2O5 Microrods from Spent Selective Catalytic Reduction Catalysts