Abstract:A detailed micromechanical finite element analysis methodology is presented to predict the transverse tensile (fiber perpendicular) failure behavior of a unidirectional (UD) glass fiber-reinforced plastic composite ply. In order to understand the constituent-level stress–strain and damage behavior, finite element analysis is accomplished using representative volume element (RVE) that consists of random fiber distribution as observed in the microscopic image of an actual composite ply. For modeling the fiber/matrix interface failure behavior, cohesive zone module (cohesive surface/cohesive element) of Abaqus® is used. In order to capture the epoxy matrix stiffness and strength degradation, the following two different approaches are used: (i) initially, the linear Drucker–Prager plasticity model in combination with a ductile fracture criterion is used; (ii) later, a brittle failure approach such as the quadratic normal stress criterion within the framework of eXtended finite element method is used. From the detailed micromechanical analysis of the RVE, it is observed that the initial damage in the RVE occurs in the form of fiber/matrix interface decohesion. With increasing tensile load, interface crack propagates and creates a stress concentration region in the matrix material, adjacent to the crack tip. Further load application causes both interface crack tip and matrix stress concentration to move away from the load application direction. As soon as the interface crack tip reaches approximately 60° to 70° away from the load application direction, the conjunction of the matrix damage with the interface crack leads to the RVE final failure. The predicted average stress–strain curves from the above-mentioned two different epoxy matrix failure criterions (ductile and brittle) correlate very well with the experimental results, indicating that the brittle failure behavior of a UD fiber-reinforced plastic composite ply under transverse tensile load is mainly controlled by the fiber/matrix interface properties.

Fracture Characteristics of Knitted Fabric Composites under Tensile Load

Tensile properties of multilayered biaxial weft knitted fabric reinforced composite material

Mechanical Deformation Mechanisms in Knitted Fabric Composites

Experimental Determination of Fracture Toughness of Woven/Chopped Glass Fiber Hybrid Reinforced Thermoplastic Composite Laminates

Elastic and Fracture Behavior of Three-Dimensional Ply-to-Ply Angle Interlock Woven Composites: Through-Thickness, Size Effect, and Multiaxial Tests

Deformation and Fracture Mechanisms of Automated Fiber Placement Pre-Preg Laminates under Out-of-plane Tensile Loading

Investigation of the translaminar fracture behavior of the fiber-reinforced composites stitched perpendicular to their plane

Effects of fabric architectures on mechanical and damage behaviors in carbon/epoxy woven composites under multiaxial stress states

Experimental Data on Fracture of Open-Hole Composite Laminates Subjected to Tension Loading

Numerical Simulation of the Mechanical Behavior of a Weft-Knitted Carbon Fiber Composite under Tensile Loading

Role of stable‐structural yarns and fabrics on the tensile and bending performance of carbon fiber resin composites

Evaluation of Tensile properties of FRP Composite Laminates under Varying Strain Rates and Temperatures

Computational micromechanical modeling of transverse tensile damage behavior in unidirectional glass fiber-reinforced plastic composite plies: Ductile versus brittle fracture mechanics approach

Evaluation and Comparison of Fracture Toughness of Glass Fibre Reinforce Composites

Fracture mechanism and fracture morphology of multi-dimensional braided carbon fiber/epoxy resin composites

Experimental investigation on the effects of fabric architectures on mechanical and damage behaviors of carbon/epoxy woven composites

Orthogonal Study on Mechanical and Tension–Tension Fatigue Properties of Flax/Glass Fiber Hybrid FRP Composites

Study on intralaminar crack propagation mechanisms in single- and multi-layer 2D woven composite laminate

The Fracture Behavior of Glass Fiber/Recycled PET Composites

Anisotropic Mechanical Response and Strain Localization of a Metallic Glassy-Fiber-Reinforced Polyethylene Terephthalate Fabric

Analysis of loading modes and rates on the mechanical responses of glass fiber weft-knitted biaxial tubular fabric reinforced composites