Investigation of the structural, electrical, and magnetic behavior of Co3+-Ti4+ doped strontium hexaferrite: validation of measured and theoretical models
Priyanka Sahu,Pradeep Kumar Sahu,Simanchalo Panigrahi
DOI: https://doi.org/10.1007/s10854-024-12356-3
2024-04-05
Journal of Materials Science Materials in Electronics
Abstract:We report the effect of Co 3+ -Ti 4+ doped SrFe 12-( x – y ) Co x Ti y O 19 ( x = y = 0.0, x = 0.225, y = 0.1125) hexaferrite successfully prepared using the conventional ceramic route. The structural, optical, electrical, and magnetic properties were analyzed via X-ray diffraction, scanning electron microscopy, diffuse reflectance spectroscopy, complex impedance spectroscopy, and vibrating sample magnetometer. The structural analysis (Rietveld Refinement) revealed that all the samples exhibit magnetoplumbite hexagonal crystal structures with P6 3 /mmc space group. At the same time, their increase in grain size and the bandgap energy showed evidence of dependency on Co 3+ -Ti 4+ content in SrFe 12 O 19 . The impedance and modulus spectra showed the suppression of surface charge polarization with substituting Co 3+ -Ti 4+ ions and co-contribution of the grain and grain boundary effect presented by modeling the electrical processes using an equivalent circuit model. Two transition peaks were observed in the temperature-dependent dielectric constant plots, represented as T d and T m . However, T m is nearly frequency-independent, and only one transition peak is identified in frequency versus dielectric constant plots. The temperature T d is due to dipole relaxation, whereas T m is assigned as dielectric phase transition, modeled by modified Curie–Weiss law. Further, the AC conductivity was examined by Jonscher's powder law and random free energy barrier model, showing that the AC conductivity increases by increasing frequency due to electronic and overlapping large-polaron hopping mechanisms. Finally, in the magnetic measurements, a simple phenomenological model was modeled based on the Lorentzian function model, representing a transition from hard to soft ferrites in the doped Co 3+ -Ti 4+ SrFe 12 O 19 with saturation magnetization of 123.66 emu/g and coercivity of 316.69 Oe.
engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied