Abstract:Commercial silica support pellets were impregnated and calcined to contain cobalt oxide and ruthenium oxide for Fischer-Tropsch synthesis (FTS). The precatalyst pellets were split evenly into two groups, the control precatalyst (c-precat) and silylated precatalyst (s-precat), which were treated with 1H,1H, 2H, 2H-perfluorooctyltriethoxysilane (PFOS) in toluene. The samples of powderized s-precat were superhydrophobic, as determined by the water droplet contact angle (>150°) and sliding angle (<1°). Thermal analysis revealed the PFOS groups to be thermally stable up to 400 °C and temperature programmed reduction (TPR) studies showed that H2 reduction of the cobalt oxide to cobalt was enhanced at lower temperatures relative to the untreated c-precat. The two active catalysts were examined for their FTS performance in a tubular fixed-bed reactor after in situ reduction at 400 °C for 16 h in flowing H2 to give the active catalysts c-cat and s-cat. The FTS runs were performed under identical conditions (255 °C, 2.1 MPa, H2/CO = 2.0, gas hourly space velocity (GHSV) 510 h–1) for 5 days. Each catalyst was examined in three runs (n = 3) and the mean values with error data are reported. S-cat showed a higher selectivity for C5+ products (64 vs. 54%) and lower selectivity for CH4 (11 vs. 17%), CO2 (2 % vs. 4 %), and olefins (8% vs. 15%) than c-cat. S-cat also showed higher CO conversion, at 37% compared to 26%, leading to a 64% increase in the C5+ productivity measured as g C5+ products per g catalyst per hour. An analysis of the temperature differential between the catalyst bed and external furnace temperature showed that s-cat was substantially more active (DTinitial = 29 °C) and stable over the 5-day run (DTfinal = 22 °C), whereas the attenuated activity of c-cat (DTinitial = 16 °C) decayed steadily over 3 days until it was barely active (DTfinal < 5 °C). A post-run surface analysis of s-cat revealed no change in the water contact angle or sliding angle, indicating that the FTS operation did not degrade the PFOS surface treatment.

Effect of TiO2 Surface Engineering on the Performance of Cobalt-Based Catalysts for Fischer–Tropsch Synthesis

Hydrothermal Carbon-Coated TiO2 As Support for Co-Based Catalyst in Fischer–Tropsch Synthesis

Uniformity Dispersive, Anti-Coking Core@double-Shell-structured Co@SiO2@C: Effect of Graphitic Carbon Modified Interior Pore-Walls on C5+ Selectivity in Fischer-Tropsch Synthesis

Self-assembly of a Highly Stable and Active Co3O4/H-TiO2 Bulk Heterojunction with High-Energy Interfacial Structures for Low Temperature CO Catalytic Oxidation

The effect of surface acidic and basic properties of highly loaded Co catalysts on the Fischer–Tropsch synthesis

Insight into the Physicochemical Properties of Co-Based Catalysts in Fischer–Tropsch Synthesis

The modification of titanium in mesoporous silica for Co-based Fischer-Tropsch catalysts

Co-Based Catalysts Supported on Silica and Carbon Materials: Effect of Support Property on Cobalt Species and Fischer–Tropsch Synthesis Performance

Effects Of Weak Surface Modification On Co/Sio2 Catalyst For Fischer-Tropsch Reaction

Design and Construction of Size-Controlled CoO/CS Catalysts for Fischer-Tropsch Synthesis

Dynamics of Co/Co2C redox cycle and their catalytic consequences in Fischer–Tropsch synthesis on cobalt–manganese catalysts

Superhydrophobic Surface Modification of a Co-Ru/SiO2 Catalyst for Enhanced Fischer-Tropsch Synthesis

Fischer–Tropsch Synthesis: Higher Oxygenate Selectivity of Cobalt Catalysts Supported on Hydrothermal Carbons

Novel Cobalt Catalysts Supported On Metal-Organic Frameworks Mil-53(Al) For The Fischer-Tropsch Synthesis

Controllable synthesis of core-shell Co@C@SiO2 catalysts for enhancing product selectivity in Fischer-Tropsch synthesis by tuning the mass transfer resistance

Tuning the Metal–Support Interaction and Enhancing the Stability of Titania-Supported Cobalt Fischer–Tropsch Catalysts via Carbon Nitride Coating

Study on Reduction Property of Cobalt Based F-T Synthesis \catalyst Supported on Alumina

The support effect on the performance of a MOF-derived Co-based nano-catalyst in Fischer Tropsch synthesis

MOFs-assisted synthesis of robust and efficient cobalt-based Fischer–Tropsch catalysts

Fischer-Tropsch Synthesis: The Characterization and Testing of Pt-Co/SiO2 Catalysts Prepared with Alternative Cobalt Precursors

Enhancing the Stability of a Cobalt-Based Fischer–Tropsch Synthesis Catalyst Using G-C3n4-coated SBA-15 As Support