Abstract:Abstract In this work, fluorine-doped tin oxide (FTO) and graphene/fluorine-doped (G-FTO) thin films were prepared using a low-cost spray pyrolysis method at a substrate temperature of 500 °C. For the FTOs, stannous chloride was dissolved in methanol and acetic acid to form the precursor solution. A 0.05 mole (M) of hydrofluoric acid was added to the precursor as an n-type impurity. The FTO thin film has an optical transmittance of 82% and electrical sheet resistance of 15 Ω/□. By meticulously integrating graphene into the optimal precursor solution of FTO, a significant improvement in the electrical conductivity of the prepared samples was achieved, leading to a reduction in the sheet resistance to 8 Ω/□ with a suitable optical transmittance of 79%. Structural, morphological, optical, and electrical properties of the prepared sample are investigated using X-ray diffraction, scanning electron microscope, UV spectroscopy, and four-point probe technique. The best performance of the FTO thin films is achieved utilizing 2.5 μmole/L of fluorine concentration at a substrate temperature of 500°C for a spraying exposer time of 20 min. The prepared sample has an electrical sheet resistance of 15 Ω/□, optical transmittance of 82%, and figure-of-merit of 91.2×10 −4 Ω −1 .The addition of 0.4 μmole/L of graphene to the optimum FTO samples enhances the performance by a remarkable reduction in the electrical the sheet resistance to 8 Ω/□ and an acceptable reduction in the optical transmittance of 79%. The overall value of the figure-of-merit increased to 118.3×10 −4 Ω −1 . The achieved results offer a high potential for adopting the prepared films for electronic and optoelectronic applications.

The Preparation and Characterization of Fluorinated Graphene Oxide with Different Degrees of Oxidation

Synthesis and Properties of Fluorinated Graphene Oxide Bisphenol a Epoxy Nanocomposites

Varying the degree of oxidation of graphite: Effect of the oxidation time and the oxidant mass

Simple Method for the Fluorinated Functionalization of Graphene Oxide

Preparation of Functionalized Graphene/thermal Conductive Polyurethane Films

Tunable Synthesis of Predominant Semi-Ionic and Covalent Fluorine Bonding States on a Graphene Surface

Preparation of Modified Fluorographene Oxide with Interlayer Supporting Structure

Oxidation modification of fluorinated graphite and its reaction mechanism

Preparation and characterization of graphene-based fluorine doped tin dioxide thin films via spray pyrolysis technique

Composition, Structure and Morphology Evolution of Octadecylamine (ODA)–Reduced Graphene Oxide and Its Dispersion Stability under Different Reaction Conditions

Water-enhanced Oxidation of Graphite to Graphene Oxide with Controlled Species of Oxygenated Groups.

Tailoring Thermal Conductivity of Bulk Graphene Oxide by Tuning the Oxidation Degree

Tuning of fluorine content in graphene: towards large-scale production of stoichiometric fluorographene

Fluorinated functionalization of graphene oxide and its role as a reinforcement in epoxy composites

Guidelines for Tailored Chemical Functionalization of Graphene

Temperature-Dependent Optical Properties of Oxidized Graphenes

Synthesis, characterization and nanoenergetic utilizations of fluorine, oxygen co-functionalized graphene by one-step XeF2 exposure

High-quality preparation of graphene oxide via the Hummers' method: Understanding the roles of the intercalator, oxidant, and graphite particle size

Covalent Synthesis of Organophilic Chemically Functionalized Graphene Sheets

Synthesis and characterizations of linear alkyl modified hydrophobic graphene oxide