Abstract:A series of graphite oxide samples were prepared using the modified Hummers method. Flake graphite was used as the raw material and the reaction temperature of the aqueous solution was changed (0 °C, 30 °C, 50 °C, 60 °C, 70 °C, 80 °C, and 100 °C). X-ray diffraction, Fourier-transform infrared spectroscopy, Raman spectral analysis, X-ray photoelectron spectroscopy, and contact angle tests were performed to characterize the structure, chemical bonding, type, and content of oxygen-containing functional groups of the graphite oxide samples. The results showed that the type and content of each oxygen-containing functional group could be controlled by changing the reaction temperature with the addition of water. As the temperature of the system increased, the degree of oxidation of the graphite oxide samples first increased and then decreased. Too high a temperature (100 °C) of the system led to the formation of epoxy groups by the decomposition of some hydroxyl groups in the samples, causing the reduction of oxygen-containing functional groups between the graphite layers, poor hydrophilic properties, and low moisture content. When the system temperature was 50 °C, the interlayer spacing of the graphite oxide samples was at its highest, the graphite was completely oxidized (C/O = 1.85), and the oxygen-containing functional groups were mainly composed of hydroxyl groups (accounting for approximately 28.88% of the total oxygen-containing functional groups). The high content of hydroxyl and carboxyl groups had good hydrophilic ability and showed the highest moisture content. The sample at 50 °C had better sensitivity to ammonia because of its high hydroxyl group and carboxyl group content, with the sample showing an excellent profile when the ammonia concentration was 20–60 ppm.

Oxidation modification of fluorinated graphite and its reaction mechanism

Mechanism of Oxidization of Graphite to Graphene Oxide by the Hummers Method.

A High-Resolution MAS NMR Study of the Structure of Fluorinated NiW/γ-Al<sub>2</sub>O<sub>3</sub>Hydrotreating Catalysts

Oxidative Aliphatic C-H Fluorination with Fluoride Ion Catalyzed by a Manganese Porphyrin

A High-Resolution MAS NMR Study of the Structure of Fluorinated NiW/γ-Al2O3 Hydrotreating Catalysts

Mechanism of catalytic ozonation in expanded graphite aqueous suspension for the degradation of organic acids

Synthesis, characterization and nanoenergetic utilizations of fluorine, oxygen co-functionalized graphene by one-step XeF2 exposure

Varying the degree of oxidation of graphite: Effect of the oxidation time and the oxidant mass

Experimental Study on the Oxidation Reaction Parameters of Different Carbon Structure Particles

Characterizing Thermal-Oxidation Behaviors of Nuclear Graphite by Combining O2 Supply and Micro Surface Area of Graphite

High-quality preparation of graphene oxide via the Hummers' method: Understanding the roles of the intercalator, oxidant, and graphite particle size

Study of the Oxidation Behavior of Fine-Grained Graphite ET-10 by Combining X-ray Μct with Mercury Porosimetry

Investigation on the Oxidation Behavior and Multi-Step Reaction Mechanism of Nuclear Graphite SNG742

Graphite oxide by "chlorate route" oxidation without HNO 3 : Does acid matter?

First Principles Study of Oxidation Behavior of Irradiated Graphite

Modeling Of Graphite Oxidation In A Stagnation-Point Flow Field Using Detailed Homogeneous And Semiglobal Heterogeneous Mechanisms With Comparisons To Experiments

Exploring Gas‐Solid Phase Diagrams: Novel Methods for Oxyfluorination of Mn3O4 and Mn2O3 with Molecular Fluorine

Investigation of oxidation behaviors of nuclear graphite being developed and IG-110 based on gas analysis

Preparation of Graphite Oxide Containing Different Oxygen-Containing Functional Groups and the Study of Ammonia Gas Sensitivity

Oxidation Experiments and Kinetics Analysis of Nuclear Graphite ET-10 by Gas Analysis and Microstructure Observation

Mechanism of Oxidation and Catalysis of Organic Matter Abiotic Humification in the Presence of MnO2